SEW 400 X55CrMo14 Soft Annealed Steel – High-Performance Cutting & Bearing Applications

Properties: - hardenable steel with high hardness and high wear resistance - resistant to water and steam with fine grounded or polished surface in hardened state - in annealed or high tempered state, corrosion resitance is not sufficient Application: - for cutting tools, like scissors, knife blades, surgical instruments - spherical for bearings, wear resistant construction parts, for control elements and parts of pumps - for stainless tools

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.58 - 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

218 - 220 GPa

100.0 °C

213 - 216 GPa

200.0 °C

206 - 209 GPa

300.0 °C

198 - 200 GPa

400.0 °C

190 - 192 GPa

500.0 °C

180 - 183 GPa

600.0 °C

167 GPa

700.0 °C

150 GPa

Hardness, Brinell

20.0 °C

260 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Martensitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Martensitic Stainless Steel

Tensile strength

20.0 °C

830 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.04E-5 - 1.05E-5 1/K

200.0 °C

1.08E-5 - 1.09E-5 1/K

300.0 °C

1.12E-5 - 1.13E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 - 1.2E-5 1/K

600.0 °C

1.22E-5 1/K

700.0 °C

1.24E-5 1/K

Melting point

1370 - 1530 °C

Typical for Martensitic Stainless Steel

Specific heat capacity

20.0 °C

430 - 439 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

492 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

700.0 °C

647 J/(kg·K)

Thermal conductivity

20.0 °C

15 - 15.7 W/(m·K)

100.0 °C

17.1 W/(m·K)

200.0 °C

18.6 W/(m·K)

300.0 °C

20 W/(m·K)

400.0 °C

21.2 W/(m·K)

500.0 °C

22.3 W/(m·K)

600.0 °C

23.1 W/(m·K)

700.0 °C

23.8 W/(m·K)

Thermal diffusivity

20.0 °C

4.7 mm²/s

100.0 °C

4.5 mm²/s

200.0 °C

4.6 mm²/s

300.0 °C

4.7 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.3 mm²/s

600.0 °C

3.7 mm²/s

700.0 °C

3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

8E-7 - 9.19E-7 Ω·m

100.0 °C

9.48E-7 Ω·m

200.0 °C

9.87E-7 Ω·m

300.0 °C

1.03E-6 Ω·m

400.0 °C

1.07E-6 Ω·m

500.0 °C

1.12E-6 Ω·m

600.0 °C

1.18E-6 Ω·m

700.0 °C

1.24E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.48 - 0.6 %

Chromium

13 - 15 %

Manganese

1 %

Molybdenum

0.5 - 0.8 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %

Vanadium

0.15 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 385 Grade Ni36 Soft Annealed (+A) – Ultra‑Low Expansion Alloy for Optics, Antennas & Measurement Tech
    2. SEW 400 X105CrMo17 Soft-Annealed Steel (+A): Superior Hardening and Wear Resistance
    3. SEW 400 X65Cr13 Stainless Steel – Soft Annealed, Superior Cutting Tool Performance
    4. SEW 400 X90CrMoV18 Soft-Annealed Steel: Superior Corrosion & Wear Resistance
    5. SEW 400 X2Cr11 Soft-Annealed Stainless Steel – Superior Corrosion Resistance & Strength
    6. SEW 400 Grade X1CrTi15 Soft Annealed Stainless Steel (+A) – High Performance Low‑Carbon Alloy for Automotive & Industrial Use
    7. SEW 400 X2CrMoNb18-2 Steel – Soft-Annealed Grade (+A) for High-Performance Applications
    8. SEW 470 Grade X3CrAlTi18-2 Soft Annealed Steel (+A): 1000 °C Resistance
    9. SEW 470 – X10CrAlSi13 Soft‑Annealed Grade for High‑Temperature Applications
    10. SEW 470: X10CrAlSi18 Soft-Annealed Steel – High-Temperature, Corrosion-Resistant Grade