SEW 400 Grade X1CrTi15 Soft Annealed Stainless Steel (+A) – High Performance Low‑Carbon Alloy for Automotive & Industrial Use

- stainless steel with estra low carbon content - for special applications in automobile industry, electro industry and homeware industry

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 - 7.73 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

217 - 220 GPa

100.0 °C

215 - 216 GPa

200.0 °C

188 - 209 GPa

300.0 °C

164 - 200 GPa

400.0 °C

192 GPa

500.0 °C

183 GPa

Elongation

20.0 °C

24 %

Hardness, Brinell

20.0 °C

180 [-]

Poisson's ratio

20.0 °C

0.29 [-]

Shear modulus

20.0 °C

84.82 GPa

Tensile strength

20.0 °C

380 - 530 MPa

Yield strength Rp0.2

20.0 °C

220 MPa

50.0 °C

215 MPa

100.0 °C

195 MPa

150.0 °C

180 MPa

200.0 °C

170 MPa

250.0 °C

160 MPa

300.0 °C

155 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.04E-5 - 1.05E-5 1/K

200.0 °C

1.08E-5 - 1.09E-5 1/K

300.0 °C

1.12E-5 - 1.13E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 - 1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

430 - 439 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

20 - 25.9 W/(m·K)

100.0 °C

25.3 W/(m·K)

200.0 °C

25.2 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.4 W/(m·K)

500.0 °C

25.7 W/(m·K)

600.0 °C

25.9 W/(m·K)

Thermal diffusivity

20.0 °C

7.6 mm²/s

100.0 °C

6.6 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.3 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.59E-7 - 7E-7 Ω·m

100.0 °C

6.4E-7 Ω·m

200.0 °C

7.32E-7 Ω·m

300.0 °C

8.17E-7 Ω·m

400.0 °C

8.97E-7 Ω·m

500.0 °C

9.74E-7 Ω·m

600.0 °C

1.05E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.015 %

Chromium

14 - 16 %

Manganese

0.5 %

Nitrogen

0.02 %

Phosphorus

0.03 %

Silicon

0.5 %

Sulfur

0.02 %

Titanium

0.25 - 0.4 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 385 Grade Ni36 Soft Annealed (+A) – Ultra‑Low Expansion Alloy for Optics, Antennas & Measurement Tech
    2. SEW 400 X105CrMo17 Soft-Annealed Steel (+A): Superior Hardening and Wear Resistance
    3. SEW 400 X65Cr13 Stainless Steel – Soft Annealed, Superior Cutting Tool Performance
    4. SEW 400 X55CrMo14 Soft Annealed Steel – High-Performance Cutting & Bearing Applications
    5. SEW 400 X90CrMoV18 Soft-Annealed Steel: Superior Corrosion & Wear Resistance
    6. SEW 400 X2Cr11 Soft-Annealed Stainless Steel – Superior Corrosion Resistance & Strength
    7. SEW 400 X2CrMoNb18-2 Steel – Soft-Annealed Grade (+A) for High-Performance Applications
    8. SEW 470 Grade X3CrAlTi18-2 Soft Annealed Steel (+A): 1000 °C Resistance
    9. SEW 470 – X10CrAlSi13 Soft‑Annealed Grade for High‑Temperature Applications
    10. SEW 470: X10CrAlSi18 Soft-Annealed Steel – High-Temperature, Corrosion-Resistant Grade