EN 1652 CuZn33 H095 – Superior Copper Alloy for Precision Engineering

CuZn33 (CW506L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn30. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn33 is used for deep drawing components, metal goods, watch parts, polishing sheet, wire mesh, cooler strips, tubular rivets and as etching brass. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

Property	Temperature	Value
Density	20.0 °C	8.5 g/cm³

Mechanical

Property	Temperature	Value
Elastic modulus	20.0 °C	112 GPa
Hardness, Vickers	20.0 °C	95 - 125 [-]
Poisson's ratio	20.0 °C	0.34 [-]
Shear modulus	20.0 °C	40 GPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Melting point		875 - 1075 °C	Typical for Wrought Copper Brass
Specific heat capacity	20.0 °C	377 J/(kg·K)
Thermal conductivity	20.0 °C	121 W/(m·K)

Electrical

Property	Temperature	Value
Electrical conductivity	20.0 °C	1.55E+7 - 1.60E+7 S/m
Electrical resistivity	20.0 °C	6.5E-8 Ω·m
Specific Electrical conductivity		28 % IACS

Chemical properties

Property	Value
Aluminium	0.02 %
Copper	66 - 68.5 %
Iron	0.05 %
Lead	0.05 %
Nickel	0.3 %
Phosphorus	0.2 %
Tin	0.1 %

EN 1652 CuZn33 (H055) Wrought Alloy – High Strength, Excellent Machinability, and Corrosion Resistance EN 1652 Grade CuZn33 H125 – Premium Unhardenable Copper Alloy for Precision Applications