EN 1652 Grade Cu-DLP H090 – Premium Deoxidized Copper Alloy
Cu-DLP, mat. No CW023A, is a deoxidized copper with limited, low residual copper-content. To the comparable DIN-make SW-Cu, mat. No 2.0076 acc. to DIN 1787 : 1973-01 applies: Tensile strength and Brinell hardness are increasable by cold forming. SW-Cu is hydrogen resistant and shows the lowest thermal and electrical conductivity of the pure copper materials. Processing properties: hot forming: very good cold forming: very good machinability: unfavorable hard soldering: very good soft soldering: very good gas-shielded welding: good burnishing: very good Application: Preferably in apparatus engineering and construction trade. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.9 - 8.94 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 129 - 132 GPa | |
Hardness, Vickers | 20.0 °C | 90 - 110 [-] | |
Poisson's ratio | 20.0 °C | 0.34 [-] | |
Shear modulus | 23.0 °C | 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper Pure / Low Alloyed Copper |
Melting point | 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 20.0 °C | 385 - 386 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 350 - 370 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 5.20E+7 S/m |
Electrical resistivity | 20.0 °C | 1.9E-8 Ω·m |
Specific Electrical conductivity | 90 % IACS |
Chemical properties
| Property | Value |
|---|---|
Bismuth | 5E-4 % |
Copper | 99.9 % |
Lead | 5E-3 % |
Phosphorus | 0.01 % |
Metal
- EN 1652 Grade Cu-DLP H040: Premium Deoxidized Copper for High-Performance Applications
- EN 1652 Grade Cu-DLP H110 – Premium Deoxidized Copper for Advanced Applications
- EN 1652 Cu-OF H090 – High-Performance Copper-Free Alloy with Superior Conductivity
- EN 1652 Grade Cu-DLP H065 – High‑Performance Deoxidized Copper
- EN 1652 Grade Cu-DLP R220: Premium Deoxidized Copper with Superior Strength
- EN 1652 Grade Cu-DLP R360 – Premium Deoxidized Copper for Superior Strength and Conductivity
- EN 1652 CuZn39Pb2 H090 Brass – Properties & Applications
- EN 1652 Cu-DLP R200 – Premium Deoxidized Copper for Superior Performance
- EN 1652 Cu-DLP R240: High-Performance Deoxidized Copper for Precision Applications
- EN 1652 Grade Cu-DLP R290 – Premium Deoxidized Copper for Industrial Use