EN 12166 CuZn36 (CW507L) – High-Strength, Unhardenable Wrought Copper Alloy

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn36 is used for deep drawing components, pressure and punching components as well as for clockfaces. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.45 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

100.0 °C

106 GPa

200.0 °C

102 GPa

300.0 °C

97 GPa

400.0 °C

89 GPa

500.0 °C

79 GPa

Hardness, Vickers

20.0 °C

190 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

700 - 800 MPa

Yield strength Rp0.2

20.0 °C

710 - 810 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

300.0 °C

2.1E-5 1/K

650.0 °C

2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

120 W/(m·K)

200.0 °C

142 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

0.02 %

Copper

63.5 - 65 %

Iron

0.05 %

Lead

0.05 %

Nickel

0.3 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12166 Grade CuZn36 R360 – Premium Beryllium Copper Alloy
    2. EN 12166 Grade CuSn5 H08 – Premium CuSn5 Tubes & Springs for Precision Engineering
    3. EN 12166: CuZn37 (H08) – High‑Performance Copper Alloy for Cold Forming and Corrosion Resistance
    4. EN 12166 Grade CuZn36 H130 – High-Performance Copper Alloy Wire
    5. EN 12166 CuZn36 H04 – Unhardenable Wrought Alloy for Precision Deep‑Drawing and Pressure Components
    6. EN 12166 Grade CuZn36 H160 – High-Performance Copper Alloy Wire
    7. EN 12166 CuZn36 (H190) – Premium Unhardenable Wrought Alloy for High‑Performance Applications
    8. CuZn36 (CW507L) – Grade EN 12166: High-Strength, Machinable Copper Alloy
    9. EN 12166 Grade H115 Copper‑Zinc Brass Wire (CuZn36) – Premium Industrial Grade
    10. EN 12166 Grade CuSn6 H08 – High-Performance Copper Tin Alloy