ASTM B316 Grade 6053 H13 – High‑Performance Aluminum Alloy Standard

Properties

General

Property	Value	Comment
Density	2.7 g/cm³	Typical for Wrought 6000 Series Aluminium

Mechanical

Property	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	70.0 GPa				Typical for Wrought 6000 Series Aluminium
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poisson's ratio	0.33 [-]				Typical for Wrought 6000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa				Typical for Wrought 6000 Series Aluminium
Tensile strength	130.0 - 180.0 MPa	H13	ASTM B316	Wire, Rod

Thermal

Property	Value	Comment
Coefficient of thermal expansion	1.6e-05 - 2.4e-05 1/K	Typical for Wrought 6000 Series Aluminium
Melting point	555.0 - 655.0 °C	Typical for Wrought 6000 Series Aluminium
Specific heat capacity	887.0 - 963.0 J/(kg·K)	Typical for Wrought 6000 Series Aluminium
Thermal conductivity	170.0 - 220.0 W/(m·K)	Typical for Wrought 6000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
Electrical resistivity	2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.15 - 0.35 %	H13	ASTM B316	Wire, Rod
Copper	0.1	H13	ASTM B316	Wire, Rod
Iron	0.35	H13	ASTM B316	Wire, Rod
Magnesium	1.1 - 1.4 %	H13	ASTM B316	Wire, Rod
Zinc	0.1	H13	ASTM B316	Wire, Rod

Technological properties

Property

Workability

Excellent workability.