ASTM A216 Grade WCC: Annealed, Normalized, or Normalized & Tempered Steel – Key Properties & Specifications
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A50 | 20.0 °C | 22 % | |
Poisson's ratio | 20.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Reduction of area | 20.0 °C | 35 % | |
Shear modulus | 20.0 °C | 75 - 80 GPa | Typical for Carbon Steel |
Tensile strength | 20.0 °C | 485 - 655 MPa | |
Yield Strength Rp0.2, short transverse | 20.0 °C | 275 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Temperature | Value | Comment |
|---|---|---|---|
Curie temperature | 20.0 °C | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.25 % |
Chromium | 0.5 % |
Copper | 0.3 % |
Manganese | 1.2 % |
Molybdenum | 0.2 % |
Nickel | 0.5 % |
Phosphorus | 0.04 % |
Silicon | 0.6 % |
Sulfur | 0.035 % |
Vanadium | 0.03 % |
Metal
- ASTM A182 Grade F6b – Annealed/Normalized & Tempered Martensitic Stainless Steel
- ASTM A420 Grade WPL6 Steel: Normalized, Tempered, Annealed or Quenched & Tempered – Specifications & Properties
- ASTM A148 Grade 1140‑1035 Steel – Properties & Heat Treatment Options
- ASTM A148 Grade 1140‑1035L Low‑Carbon Steel: Properties for Annealed, Normalized, Tempered, and Quenched Treatments
- ASTM A148 Grade 1450–1240 Steel: Properties & Heat Treatment Options
- ASTM A148 Grade 1450-1240L Steel – Annealed, Normalized, Tempered or Quenched & Tempered
- ASTM A148 Grade 1795‑1450: High‑Strength Low‑Carbon Steel – Annealed, Normalized, or Quenched & Tempered
- ASTM A148 Grade 1795–1450L Steel: Annealed, Normalized, Tempered, or Quenched & Tempered – Performance Overview
- ASTM A148 Grade 550–275 Steel – Comprehensive Guide to Annealed, Normalized, and Tempered Conditions
- ASTM A216 Grade WCA Steel – Annealed, Normalized, or Normalized & Tempered Specifications