CuZn37 Hard Brass – Durable, Antimicrobial Sheet & Foil
Brass with antimicrobial properties
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.4 g/cm³ |
Dimension
| Property | Value |
|---|---|
Dimensions | Sheet Thickness: 0.3 - 8 mm, Foil Thickness: 0.005-0.45 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 110 GPa |
Elongation A5 | 23.0 °C | 12 % |
Hardness, Brinell | 23.0 °C | 190 [-] |
Tensile strength | 23.0 °C | 610 MPa |
Yield strength Rp0.2 | 23.0 °C | 580 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.02E-5 1/K |
Thermal conductivity | 23.0 °C | 121 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 1.55E+7 S/m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 62 - 64 % |
Iron | 0.1 % |
Lead | 0.1 % |
Nickel | 0.3 % |
Tin | 0.1 % |
High-Temperature Tungsten Ground Rod for Superior Stability
DIN 17744 Grade NiMo16Cr16Ti – Heat‑Treated & Quenched for Optimal Performance
Metal
- Industrial Hard Hats: Standards, History, and Future Trends
- Learning 3D Printing Made Simple: A Beginner's Guide
- Rhodium (Rh): Properties, Hardness, and Applications
- EN 12167 CuZn37 R400 – Premium Cold‑Formed Copper Alloy
- EN 1652 Grade CuZn37 H115 – High-Strength, Cold-Formable Copper Alloy
- EN 12163 Grade CuZn37 H105 – High-Performance Unhardenable Copper Alloy
- Platinum (Pt) – Properties, Applications, and Industrial Significance
- CuZn37 Soft Brass: Antimicrobial, High Strength & Versatile
- What Is Hard Turning? A Deep Dive into Precision Machining.
- Hard Turning: The Key to Precise Machining of High-Hardness Materials