SEW 410: G-X2CrNiMoN18-10 Quenched Stainless Steel – Superior Corrosion Resistance
G-X 2 CrNiMoN 18 10, for cast parts with increased resistance against intercristalline corrosion. no treatment after welding necessary
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 195 GPa | Typical for Austenitic Stainless Steel |
Elongation | 20.0 °C | 30 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Austenitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 20.0 °C | 440 - 640 MPa | |
Yield strength Rp0.2 | 20.0 °C | 205 MPa | |
100.0 °C | 140 MPa | ||
200.0 °C | 110 MPa | ||
300.0 °C | 92 MPa | ||
350.0 °C | 85 MPa | ||
400.0 °C | 80 MPa | ||
Yield strength Rp1.0 | 20.0 °C | 230 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.65E-5 1/K | |
200.0 °C | 1.75E-5 1/K | ||
300.0 °C | 1.75E-5 1/K | ||
400.0 °C | 1.85E-5 1/K | ||
Melting point | 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 15 W/(m·K) | |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.03 % |
Chromium | 17 - 20 % |
Manganese | 1.5 % |
Molybdenum | 2 - 3 % |
Nickel | 9 - 13 % |
Nitrogen | 0.1 - 0.2 % |
Phosphorus | 0.04 % |
Silicon | 1.5 % |
Sulfur | 0.02 % |
Metal
- SEW 410 Grade G-X3CrNiMoN26-6-3 Quenched (+Q) – Enhanced Corrosion Resistance for Pump Components
- SEW 410 Grade G-X2CrNiMoN25-7-4 Quenched Steel for High‑Performance Pump Components
- SEW 410 Grade G‑X3CrNiMoCuN26‑6‑3‑3 – Quenched ( +Q ) Stainless Steel with Superior Corrosion Resistance
- SEW 410 Grade G-X5CrNiMo16-5: Quenched & Tempered Martensitic Stainless Steel for High-Performance Applications
- SEW 410 G-X2CrNiN18-9 Quenched Stainless Steel – High Corrosion Resistance
- SEW 410 Grade G-X8CrNi26-7 – High Toughness Duplex Stainless Steel, Quenched (+Q)
- SEW 400 X2CrNiN18-7 Quenched Stainless Steel – High Strength & Corrosion Resistance
- SEW 400 X4CrNiMoN27-5-2 Quenched Steel: High Performance & Corrosion Resistance
- SEW 410 Grade G-X 2 NiCrMoCuN25-20 – Quenched Alloy for High-Temperature Pump Components
- SEW 400 Grade X12CrNi17-7 – Quenched Stainless Steel for High-Strength, Corrosion-Resistant Automotive Applications