SEW 400 X2CrNiN18-7 Quenched Stainless Steel – High Strength & Corrosion Resistance

- high strength stainless extra low carbon steel for special applications - corrosion resistance is similar to 1.4311

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.92 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 198 GPa

100.0 °C

190 - 192 GPa

200.0 °C

182 - 183 GPa

300.0 °C

174 - 175 GPa

400.0 °C

166 - 167 GPa

500.0 °C

150 - 158 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

40 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

600 - 900 MPa

Yield strength Rp0.2

20.0 °C

350 MPa

Yield strength Rp1.0

20.0 °C

380 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.64E-5 - 1.67E-5 1/K

200.0 °C

1.72E-5 - 1.89E-5 1/K

300.0 °C

1.74E-5 - 1.77E-5 1/K

400.0 °C

1.78E-5 - 1.81E-5 1/K

500.0 °C

1.82E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

450 - 472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

-100.0 °C

11.7 W/(m·K)

20.0 °C

14.5 - 15 W/(m·K)

100.0 °C

16 W/(m·K)

200.0 °C

17.6 W/(m·K)

300.0 °C

19.1 W/(m·K)

400.0 °C

20.4 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.7 W/(m·K)

800.0 °C

26.1 W/(m·K)

Thermal diffusivity

-100.0 °C

3.7 mm²/s

20.0 °C

3.9 mm²/s

100.0 °C

4.3 mm²/s

200.0 °C

4.3 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

5.86E-7 Ω·m

20.0 °C

6.92E-7 - 8E-7 Ω·m

100.0 °C

7.58E-7 Ω·m

200.0 °C

8.36E-7 Ω·m

300.0 °C

9.07E-7 Ω·m

400.0 °C

9.73E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.06E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.13E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Nickel

6 - 8 %

Nitrogen

0.1 - 0.15 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 400 X4CrNiMoN27-5-2 Quenched Steel: High Performance & Corrosion Resistance
    2. SEW 400 Grade X12CrNi17-7 – Quenched Stainless Steel for High-Strength, Corrosion-Resistant Automotive Applications
    3. SEW 400 Grade X1CrNiMoTi18-13-2 – High-Performance Quenched Stainless Steel for Elevated Temperature Applications
    4. SEW 400 X3CrNiMoTi25-25 Quenched Steel – High Corrosion Resistance for Chemical & Textile Industries
    5. SEW 400 X1CrNi25-21 Quenched Steel – High Corrosion Resistance & Structural Integrity
    6. SEW 400 Duplex Stainless Steel (X2CrNiN23-4) – Quenched for Superior Strength and Corrosion Resistance
    7. SEW 400 X2CrNiMoN22-5-3 Quenched Steel – High Corrosion Resistance & Superior Weldability
    8. SEW 400 Grade X2CrNiMnMoNbN25-18-5-4 Quenched Alloy – Premium Strength & Corrosion Resistance
    9. SEW 400 X1NiCrMoCuN25-20-6 Quenched Steel – Superior Corrosion Resistance for Offshore Applications
    10. SEW 400 X1NiCrMoCuN31-27-4 Quenched Steel (+Q) – Superior Corrosion Resistance for Chemical Applications