SEW 400 X1NiCrMoCuN25-20-6 Quenched Steel – Superior Corrosion Resistance for Offshore Applications

-100.0 °C

206 GPa

20.0 °C

196 - 198 GPa

100.0 °C

190 - 193 GPa

200.0 °C

182 - 183 GPa

300.0 °C

174 - 175 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 159 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

20.0 °C

270 MPa

50.0 °C

240 MPa

100.0 °C

230 MPa

150.0 °C

210 MPa

200.0 °C

190 MPa

250.0 °C

180 MPa

300.0 °C

170 MPa

350.0 °C

160 MPa

400.0 °C

140 MPa

450.0 °C

130 MPa

500.0 °C

120 MPa

550.0 °C

105 MPa

20.0 °C

310 MPa

50.0 °C

280 MPa

100.0 °C

270 MPa

150.0 °C

245 MPa

200.0 °C

225 MPa

250.0 °C

215 MPa

300.0 °C

205 MPa

350.0 °C

190 MPa

400.0 °C

170 MPa

450.0 °C

160 MPa

500.0 °C

150 MPa

550.0 °C

135 MPa

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.58E-5 - 1.67E-5 1/K

200.0 °C

1.61E-5 - 1.72E-5 1/K

300.0 °C

1.65E-5 - 1.77E-5 1/K

400.0 °C

1.69E-5 - 1.81E-5 1/K

500.0 °C

1.73E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

-100.0 °C

440 J/(kg·K)

20.0 °C

450 - 472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

20.0 °C

11.9 - 12 W/(m·K)

100.0 °C

13.3 W/(m·K)

200.0 °C

15.1 W/(m·K)

300.0 °C

16.7 W/(m·K)

400.0 °C

18.3 W/(m·K)

500.0 °C

19.8 W/(m·K)

600.0 °C

21.3 W/(m·K)

700.0 °C

22.8 W/(m·K)

800.0 °C

24.3 W/(m·K)

900.0 °C

25.7 W/(m·K)

1000.0 °C

27.1 W/(m·K)

20.0 °C

3.3 mm²/s

100.0 °C

3.4 mm²/s

200.0 °C

3.7 mm²/s

300.0 °C

4.1 mm²/s

400.0 °C

4.3 mm²/s

500.0 °C

4.5 mm²/s

600.0 °C

4.7 mm²/s

700.0 °C

5 mm²/s

800.0 °C

5.4 mm²/s

900.0 °C

5.7 mm²/s

1000.0 °C

5.8 mm²/s