SEW 410 Grade G-X5CrNiMo16-5: Quenched & Tempered Martensitic Stainless Steel for High-Performance Applications
G-X 5 CrNiMo 16 5, for cast parts with increased strength, toughness and corrosion resistance, used for water turbines, pumps, armatures, compressors, ship propellers.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa | Typical for Martensitic Stainless Steel |
Elongation | 20.0 °C | 15 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Martensitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 760 - 960 MPa | |
Yield strength Rp0.2 | 20.0 °C | 540 MPa | |
100.0 °C | 515 MPa | ||
200.0 °C | 485 MPa | ||
300.0 °C | 455 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.1E-5 1/K | |
200.0 °C | 1.2E-5 1/K | ||
300.0 °C | 1.25E-5 1/K | ||
400.0 °C | 1.3E-5 1/K | ||
500.0 °C | 1.35E-5 1/K | ||
Melting point | 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 25 W/(m·K) | |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.07 % |
Chromium | 15 - 16.5 % |
Manganese | 1 % |
Molybdenum | 0.5 - 2 % |
Nickel | 4.5 - 6 % |
Phosphorus | 0.04 % |
Silicon | 1 % |
Sulfur | 0.025 % |
Metal
- SEW 555 27NiCrMoV11-6 Quenched & Tempered Steel – High-Performance Turbine & Generator Shafts
- SEW 835 GS-Ck45 Quenched & Tempered Steel for High-Performance Mechanical Components
- SEW 835 Grade GS-C45 Quenched & Tempered Steel for Mechanical Engineering Applications
- SEW 835 GS-36Mn5 Quenched & Tempered Steel – High Strength & Durability
- SEW 555 30CrMoNiV5‑11 Steel – High‑Strength Quenched & Tempered for Turbine Shafts & Discs
- SEW 555 28CrMoNiV4-9: Quenched & Tempered Alloy Steel for Turbine Shafts & Discs
- SEW 555 X14CrMoVNbN10-1 Quenched & Tempered Steel – High‑Performance Turbine & Generator Components
- SEW 555: 23CrNiMo7-4-7 Quenched & Tempered Alloy Steel for High-Performance Turbine Shafts and Discs
- SEW 555 X12CrMoWVNbN10-1-1 Quenched & Tempered Steel – High-Performance Turbine Shafts
- SEW 400 Grade X35CrMo17 Quenched & Tempered Steel: High Performance & Corrosion Resistance