SEW 835 GS-36Mn5 Quenched & Tempered Steel – High Strength & Durability
Application preferably for welded components, e.g. chain links for undercarriages.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Medium Carbon Steel |
Elongation | 20.0 °C | 17 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Medium Carbon Steel |
Shear modulus | 23.0 °C | 75 - 80 GPa | Typical for Carbon Steel |
Tensile strength | 20.0 °C | 540 MPa | |
Yield strength | 20.0 °C | 314 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 1/K | Typical for Medium Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1380 - 1514 °C | Typical for Medium Carbon Steel | |
Specific heat capacity | 23.0 °C | 470 - 520 J/(kg·K) | Typical for Medium Carbon Steel |
Thermal conductivity | 23.0 °C | 21 - 52 W/(m·K) | Typical for Medium Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.32 - 0.4 % |
Manganese | 1.2 - 1.5 % |
Phosphorus | 0.04 % |
Silicon | 0.25 - 0.5 % |
Sulfur | 0.035 % |
Metal
- SEW 410 Grade G-X5CrNiMo16-5: Quenched & Tempered Martensitic Stainless Steel for High-Performance Applications
- SEW 555 27NiCrMoV11-6 Quenched & Tempered Steel – High-Performance Turbine & Generator Shafts
- SEW 835 GS-Ck45 Quenched & Tempered Steel for High-Performance Mechanical Components
- SEW 835 Grade GS-C45 Quenched & Tempered Steel for Mechanical Engineering Applications
- SEW 555 30CrMoNiV5‑11 Steel – High‑Strength Quenched & Tempered for Turbine Shafts & Discs
- SEW 555 28CrMoNiV4-9: Quenched & Tempered Alloy Steel for Turbine Shafts & Discs
- SEW 555 X14CrMoVNbN10-1 Quenched & Tempered Steel – High‑Performance Turbine & Generator Components
- SEW 555: 23CrNiMo7-4-7 Quenched & Tempered Alloy Steel for High-Performance Turbine Shafts and Discs
- SEW 555 X12CrMoWVNbN10-1-1 Quenched & Tempered Steel – High-Performance Turbine Shafts
- SEW 400 Grade X35CrMo17 Quenched & Tempered Steel: High Performance & Corrosion Resistance