SEW 400 Grade X35CrMo17 Quenched & Tempered Steel: High Performance & Corrosion Resistance

Properties: - Cr-steel for quenching and tempering - elevated corrosion resistance - widely resistant in most organic and inorganic acids - relatively resistant in seawater - improved resistance to crevice corrosion - elevated heat resistance up to 600 °C - high polishable - use differnent quenched and tempered grad in case of sliding contact - application temperature: -40 to 550 °C - excellent runnability and wear resistance Application: - for pump axis, sindle, fittings, beater bar

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.56 - 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

218 - 223 GPa

100.0 °C

213 - 216 GPa

200.0 °C

206 - 209 GPa

300.0 °C

198 - 200 GPa

400.0 °C

190 - 192 GPa

500.0 °C

180 - 183 GPa

600.0 °C

167 GPa

700.0 °C

150 GPa

Elongation

20.0 °C

10 - 12 %

Hardness, Brinell

20.0 °C

235 - 285 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Martensitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Martensitic Stainless Steel

Tensile strength

20.0 °C

750 - 950 MPa

Yield strength Rp0.2

20.0 °C

550 MPa

50.0 °C

550 MPa

100.0 °C

550 MPa

150.0 °C

540 MPa

200.0 °C

530 MPa

250.0 °C

520 MPa

300.0 °C

510 MPa

350.0 °C

490 MPa

400.0 °C

470 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

9.9E-6 1/K

100.0 °C

1.03E-5 - 1.04E-5 1/K

200.0 °C

1.08E-5 1/K

300.0 °C

1.12E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 1/K

600.0 °C

1.21E-5 1/K

700.0 °C

1.24E-5 1/K

800.0 °C

1.29E-5 1/K

Max service temperature, long

-40 - 550 °C

Melting point

1370 - 1530 °C

Typical for Martensitic Stainless Steel

Specific heat capacity

20.0 °C

430 - 450 J/(kg·K)

100.0 °C

482 J/(kg·K)

200.0 °C

506 J/(kg·K)

300.0 °C

525 J/(kg·K)

400.0 °C

547 J/(kg·K)

500.0 °C

576 J/(kg·K)

600.0 °C

616 J/(kg·K)

Thermal conductivity

20.0 °C

15 - 16 W/(m·K)

100.0 °C

17.2 W/(m·K)

200.0 °C

18.6 W/(m·K)

300.0 °C

20 W/(m·K)

400.0 °C

21.2 W/(m·K)

500.0 °C

22.3 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.1 W/(m·K)

800.0 °C

25.5 W/(m·K)

900.0 °C

26.9 W/(m·K)

1000.0 °C

28.3 W/(m·K)

Thermal diffusivity

20.0 °C

4.7 mm²/s

100.0 °C

4.5 mm²/s

200.0 °C

4.5 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.4 mm²/s

500.0 °C

4.1 mm²/s

600.0 °C

3.6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

8E-7 - 9.06E-7 Ω·m

100.0 °C

9.42E-7 Ω·m

200.0 °C

9.87E-7 Ω·m

300.0 °C

1.03E-6 Ω·m

400.0 °C

1.08E-6 Ω·m

500.0 °C

1.12E-6 Ω·m

600.0 °C

1.18E-6 Ω·m

700.0 °C

1.22E-6 Ω·m

800.0 °C

1.24E-6 Ω·m

900.0 °C

1.26E-6 Ω·m

1000.0 °C

1.27E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.33 - 0.45 %

Chromium

15.5 - 17.5 %

Manganese

1 %

Molybdenum

0.8 - 1.3 %

Nickel

1 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 410 Grade G-X5CrNiMo16-5: Quenched & Tempered Martensitic Stainless Steel for High-Performance Applications
    2. SEW 555 27NiCrMoV11-6 Quenched & Tempered Steel – High-Performance Turbine & Generator Shafts
    3. SEW 835 GS-Ck45 Quenched & Tempered Steel for High-Performance Mechanical Components
    4. SEW 835 Grade GS-C45 Quenched & Tempered Steel for Mechanical Engineering Applications
    5. SEW 835 GS-36Mn5 Quenched & Tempered Steel – High Strength & Durability
    6. SEW 555 30CrMoNiV5‑11 Steel – High‑Strength Quenched & Tempered for Turbine Shafts & Discs
    7. SEW 555 28CrMoNiV4-9: Quenched & Tempered Alloy Steel for Turbine Shafts & Discs
    8. SEW 555 X14CrMoVNbN10-1 Quenched & Tempered Steel – High‑Performance Turbine & Generator Components
    9. SEW 400 – X2CrNiMo13‑4 Steel, Quenched & Tempered (QT) – High‑Performance Corrosion‑Resistant Grade
    10. SEW 400 Grade X20CrMo13: Quenched & Tempered Steel for High-Temperature Applications