SEW 101 Grade 27MnSiVS6 – Hot-Worked, Controlled-Cooled Steel for Automotive Forgings

The ferritic-pearlitic, precipitation hardened steel 27 MnSiVS 6 is used for forgings in the automotive industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

14 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Manganese Steel

Reduction of area

20.0 °C

30 %

Tensile strength

20.0 °C

800 - 950 MPa

Yield strength

20.0 °C

500 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Manganese Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

42.5 W/(m·K)

100.0 °C

43.5 W/(m·K)

200.0 °C

42.8 W/(m·K)

300.0 °C

40.9 W/(m·K)

400.0 °C

39 W/(m·K)

500.0 °C

36.4 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.7 mm²/s

100.0 °C

11.2 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.3 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.45E-7 Ω·m

100.0 °C

2.94E-7 Ω·m

200.0 °C

3.69E-7 Ω·m

300.0 °C

4.59E-7 Ω·m

400.0 °C

5.58E-7 Ω·m

500.0 °C

6.79E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.25 - 0.3 %

Manganese

1.3 - 1.6 %

Phosphorus

0.04 %

Silicon

0.5 - 0.8 %

Sulfur

0.03 - 0.05 %

Vanadium

0.08 - 0.13 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. SEW 395 Grade GX12CrNi18-11: High‑Performance Austenitic Steel, Heat‑Treated & Quenched
    2. SEW 410 Grade G-X5CrNiMo16-5: Quenched & Tempered Martensitic Stainless Steel for High-Performance Applications
    3. SEW 555 27NiCrMoV11-6 Quenched & Tempered Steel – High-Performance Turbine & Generator Shafts
    4. SEW 835 GS-Ck45 Quenched & Tempered Steel for High-Performance Mechanical Components
    5. SEW 101: Grade 38MnSiVS5 Hot‑Worked and Controlled‑Cooled Steel – High‑Performance Automotive Forgings
    6. SEW 101 Grade 44MnSiVS6: Hot‑Worked and Controlled‑Cooled Steel for Automotive Forgings
    7. SEW 101 Grade 49MnVS3 – Hot-Worked, Controlled-Cooled Steel for Automotive Forgings
    8. DIN 1630 Grade St 37.4 Hot-Worked & Normalized Seamless Tubes – High Strength & Weldability
    9. DIN 1630 Grade St 44.4: Hot-Worked, Normalized Steel Tubes for High-Performance Applications
    10. DIN 1630 Grade St 52.4 – Hot-Worked, Normalized Seamless Tubes for High-Temperature Applications