AMPCO® 25 Forgings: High-Performance Alloy for Superior Die Materials

AMPCO® 25 is a patented alloy which displays outstanding mechanical properties. The extreme hardness, linked with an excellent compressive strength and very good friction properties, makes it ideal as a forming and drawing die material. As the elongation of the material is nil, thin sections should be avoided and the material should be well backed up.

Properties

General

Property	Temperature	Value
Density	23.0 °C	6.93 g/cm³
Recycled Content		80 %

Mechanical

Property	Temperature	Value	Comment
Compressive strength	23.0 °C	1579 MPa
Compressive yield strength, 0.1%	23.0 °C	706 MPa
Elastic modulus	23.0 °C	110 GPa
Hardness, HBW	23.0 °C	375 [-]	HBW 10/3000
Hardness, Rockwell C	23.0 °C	40 [-]
Shear strength	23.0 °C	451 MPa

Thermal

Property	Temperature	Value
Coefficient of thermal expansion	23.0 °C	1.62E-5 1/K
Specific heat capacity	23.0 °C	420 J/(kg·K)
Thermal conductivity	23.0 °C	33 W/(m·K)

Electrical

Property	Temperature	Value
Electrical conductivity	23.0 °C	4.00E+6 S/m
Specific Electrical conductivity		8 % IACS

Chemical properties

Property	Value
Copper	Balance

Technological properties

Property
Application areas	The phenomenal success of this alloy led to its use as forming rolls, bending and wiping blocks and it is considered the standard material in this field of applications. Due to its inherent friction properties, this alloy has an excellent behaviour in any wear application where high compression loads are present.