DIN 5513 AW‑5754: Premium Rail Vehicle Material – High Strength, Corrosion Resistance & Anodizable

Application note for rail vehicles (according to DIN 5513 for H111, H112, H12, H22 conditions): - for roof and side walls - observe the decrease in strength in heat affected zone in H112, H12 and H22 conditions - good chemical resistance, good cold formability in the H111, H112 and H22 conditions The material can be anodised.

Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

Properties

General

Property	Value
Density	2.67 g/cm³

Mechanical

Property	Value	Comment
Elastic modulus	70.0 GPa
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m	Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]	Typical for Wrought 5000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa	Typical for Wrought 5000 Series Aluminium
Tensile strength	115.0 MPa
Yield strength	80.0 MPa

Thermal

Property	Value	Comment
Coefficient of thermal expansion	2.3800000000000003e-05 1/K
Max service temperature	150.0 °C	Typical for Wrought 5000 Series Aluminium
Melting point	560.0 - 655.0 °C	Typical for Wrought 5000 Series Aluminium
Specific heat capacity	900.0 J/(kg·K)
Thermal conductivity	145.0 W/(m·K)

Electrical

Property	Value	Comment
Electrical conductivity	18000000.0 - 31000000.0 S/m	Typical for Wrought 5000 Series Aluminium
Electrical resistivity	3.3e-08 - 5e-08 Ω·m	Typical for Wrought 5000 Series Aluminium

Technological properties

Property
Workability	Good workability.

Property

Workability

Good workability.