EN 10083-2 Grade C60R Quenched & Tempered Steel – High Strength & Workability for Automotive & Industrial Applications

Steel C60R is suitable for high loaded parts in vehicle manufacturing, engine and machine engineering requiring improved workability while maintaining constant strength properties (e.g. gear wheels, pinions, shafts). As a bright steel product it is used in the form of bars, bright, straight, in different conditions (see DIN EN 10277).

Properties

General

Property	Temperature	Value
Density	20.0 °C	7.85 g/cm³

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	20.0 °C	210 GPa
	100.0 °C	205 GPa
	200.0 °C	195 GPa
	300.0 °C	185 GPa
	400.0 °C	175 GPa

Elongation	20.0 °C	11 - 14 %
Poisson's ratio	23.0 °C	0.29 [-]	Typical for High Carbon Steel
Reduction of area	20.0 °C	25 - 35 %
Shear modulus	20.0 °C	81 GPa
Tensile strength	20.0 °C	750 - 1000 MPa
Yield strength	20.0 °C	450 - 580 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	100.0 °C	1.11E-5 1/K
	200.0 °C	1.21E-5 1/K
	300.0 °C	1.29E-5 1/K
	400.0 °C	1.35E-5 1/K

Max service temperature		500 °C	Typical for Carbon Steel
Melting point		1289 - 1478 °C	Typical for High Carbon Steel
Specific heat capacity	23.0 °C	486 J/(kg·K)	Typical for High Carbon Steel
Thermal conductivity	20.0 °C	51 W/(m·K)
	100.0 °C	49.9 W/(m·K)
	200.0 °C	47.8 W/(m·K)
	300.0 °C	44.8 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	20.0 °C	1.3E-7 Ω·m

Chemical properties

Property	Value
Carbon	0.57 - 0.65 %
Chromium	0.4 %
Copper	0.3 %
Manganese	0.6 - 0.9 %
Molybdenum	0.1 %
Nickel	0.4 %
Phosphorus	0.03 %
Silicon	0.1 - 0.4 %
Sulfur	0.02 - 0.04 %

EN 10083-2 Grade C55R - Normalized or Normalized Formed Steel for High-Performance Applications EN 10083-2 Grade 28Mn6 Steel – Quenched & Tempered for Automotive & Machine Applications