EN 10269 Grade 25CrMo4 Quenched & Tempered: Premium High‑Strength Steel

Steel 25CrMo4 is suitable for components with high strength and toughness requirements at mean and higher heat-treatment cross-sections in vehicle, engine and machine engineering (e.g. crankshafts, steering knuckles, pinions). Lowest working temperature -40 °C Further application for mounting elements at increased and lower temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

18 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Reduction of area

20.0 °C

60 %

Tensile strength

20.0 °C

600 - 750 MPa

300.0 °C

460 MPa

350.0 °C

440 MPa

Yield strength Rp0.2

20.0 °C

420 - 440 MPa

50.0 °C

414 - 435 MPa

100.0 °C

403 - 428 MPa

150.0 °C

393 - 420 MPa

200.0 °C

382 - 412 MPa

250.0 °C

372 - 392 MPa

300.0 °C

344 - 363 MPa

350.0 °C

324 - 333 MPa

400.0 °C

294 - 304 MPa

450.0 °C

265 - 275 MPa

500.0 °C

226 - 235 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 200 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41 W/(m·K)

100.0 °C

11.1 - 42.7 W/(m·K)

200.0 °C

12.1 - 42.8 W/(m·K)

300.0 °C

12.9 - 41.6 W/(m·K)

400.0 °C

39.9 W/(m·K)

500.0 °C

37.8 W/(m·K)

600.0 °C

35.6 W/(m·K)

Thermal diffusivity

20.0 °C

11.4 mm²/s

100.0 °C

11 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.5 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.54E-7 Ω·m

100.0 °C

3E-7 Ω·m

200.0 °C

3.69E-7 Ω·m

300.0 °C

4.51E-7 Ω·m

400.0 °C

5.45E-7 Ω·m

500.0 °C

6.54E-7 Ω·m

600.0 °C

7.78E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.22 - 0.29 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10297-1 Grade 25CrMo4 Quenched & Tempered Steel – Properties & Applications
    2. EN 10132-3: 25CrMo4 Quenched & Tempered Cold-Rolled Strip – Precision Steel for Industrial Applications
    3. EN 10269 21CrMoV5-7 Quenched & Tempered Steel – Superior High-Temperature Strength
    4. EN 10269 Grade 30CrNiMo8 – High‑Performance Quenched & Tempered Steel for Aircraft & Heavy Machinery
    5. EN 10269 Grade 34CrNiMo6 – Quenched & Tempered (QT) Steel for High-Stress Applications
    6. EN 10269 40CrMoV4-6 Quenched & Tempered Steel – High‑Temperature Performance up to 540 °C
    7. EN 10269 Grade 42CrMo4 Quenched & Tempered (QT) – High‑Performance Steel for Heavy‑Duty Applications
    8. EN 10269 X12CrNiMoV12-3 Quenched & Tempered Steel – Martensitic Stainless for Turbine Applications
    9. EN 10263-4 Grade 25CrMo4 Quenched & Tempered Steel – High Strength, Cold-Formable
    10. EN 10269 Grade X19CrMoNbVN11-1 - Quenched & Tempered Steel for High-Temperature Applications