UNS R56410 Titanium Beta Alloy – Superior Strength & Heat‑Treatability
This alloy UNS R56410 is a Titanium Beta Alloy. It is harder and stronger than many titanium alloys. This Titanium is a heat treatable alloy, it’s weldable and it’s easily formed. The chief problems for this alloy include flank wear, spring-back and chip control. Because of these characteristics, positive rake chip grooves in combination with light hones on the cutting edge are advantageous.
Properties
General
| Property | Value | Shape |
|---|---|---|
Density | 4.65 g/cm³ | Bar, Billet |
Dimension
| Property | Temperature | Value | Shape | Comment |
|---|---|---|---|---|
Diameter | 7 mm | Bar | ||
115 mm | Bar | |||
130 mm | Billet | |||
350 mm | Billet | |||
Dimensions | 15-65 mm diameter up to 6000 mm length °C | 7-14.5 mm diameter up to 3000 mm length | Bar | |
Length | 3000 mm | Billet | ||
4500 mm | Billet | |||
6000 mm | Bar | max |
Mechanical
| Property | Value | Shape |
|---|---|---|
Elastic modulus | 110.0 | Bar, Billet |
Elongation | 9.0 % | Bar, Billet |
Hardness, Brinell | 304.0 | Bar, Billet |
Hardness, Rockwell C | 32.0 [-] | Bar, Billet |
Hardness, Vickers | 318.0 | Bar, Billet |
Shear modulus | 41.0 GPa | Bar, Billet |
Tensile strength | 970.0 MPa | Bar, Billet |
Yield strength | 900.0 MPa | Bar, Billet |
Thermal
| Property | Value | Shape | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 7.099999999999997e-06 - 9.699999999999999e-06 1/K | Typical for Titanium Beta Alloy | |
Melting point | 1550.0 - 1815.0 °C | Typical for Titanium Beta Alloy | |
Specific heat capacity | 490.0 - 580.0 J/(kg·K) | Typical for Titanium Beta Alloy | |
Thermal conductivity | 7.8 W/(m·K) | Bar, Billet |
Chemical properties
| Property | Value | Shape |
|---|---|---|
Aluminium | 2.6 - 3.4 % | Bar, Billet |
Carbon | 0.05 % | Bar, Billet |
Hydrogen | 0.015 | Bar, Billet |
Iron | 1.6 - 2.2 % | Bar, Billet |
Nitrogen | 0.05 | Bar, Billet |
Oxygen | 0.13 | Bar, Billet |
Vanadium | 9.0 - 11.0 % | Bar, Billet |
Metal
- Corrosion‑Resistant Zirconium Alloys: Key Properties & Applications
- Alloy 31 Stainless Steel Plate – Superior Strength & Ductility for Extreme Environments
- ASTM Alloy 20 Heat‑Treated Stainless Steel – Properties & Performance
- FeNi42 Alloy: Low Thermal Expansion for Precision Seals
- UNS S31803 Duplex Stainless Steel Plate – High Strength & Corrosion Resistance
- Alloy 718 – High‑Performance Nickel‑Chromium Steel
- AA 2219 T3 Aluminum Alloy – Superior Strength & Heat Resistance
- AA 2219 T8 Aluminum Alloy – High Strength, Heat‑Resistant, Ideal for Advanced Metalworking
- Alloy 52 Plate – High-Performance Nickel-Iron Composite for Industrial Applications
- Alloy 52 Bar: High-Performance Nickel-Iron Steel with Superior Strength