EN 12165 Grade CuZn39Pb2 H080 Brass – Specifications & Applications

Material CuZn39Pb2, mat. No. CW612N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb2, mat. No. 2.0380 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: For components in precision mechanics, machine and apparatus engineering as well as for circuit boards and clockwerks for watch industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.45 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

102 GPa

Hardness, Brinell

20.0 °C

80 [-]

Hardness, Vickers

20.0 °C

80 - 110 [-]

Poisson's ratio

20.0 °C

0.34 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

350 MPa

Yield strength Rp0.2

20.0 °C

140 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

2E-5 1/K

300.0 °C

2.1E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

20.0 °C

109 - 117 W/(m·K)

200.0 °C

134 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.39E+7 - 1.40E+7 S/m

200.0 °C

1.10E+7 S/m

Electrical resistivity

20.0 °C

7.1E-8 Ω·m

200.0 °C

9.1E-8 Ω·m

Specific Electrical conductivity

24 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Copper

59 - 60 %

Iron

0.3 %

Lead

1.6 - 2.5 %

Nickel

0.3 %

Tin

0.3 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12164 Grade CuZn39Pb2 M – Lead-Enhanced Brass Alloy for Durable Applications
    2. EN 12165 Grade CuBe2 M – Premium Hardenable Copper Alloy for High Strength and Durability
    3. EN 12166 Grade CuZn36Pb3 H080 – High-Performance Copper Alloy Wire
    4. EN 1652 Grade CuZn39Pb2 H150 – Premium Lead-Added Brass Alloy
    5. EN 1652 Grade CuZn39Pb2 H175: Lead‑Enhanced Brass for Superior Machinability and Strength
    6. EN 1652 Grade CuZn10 H080 – High-Performance Wrought Copper Alloy
    7. EN 12165 Grade CuZn39Pb0.5 H080 – High‑Strength Leaded Brass Alloy
    8. EN 12165 Copper Alloy Wire – CuZn38Pb2 H080 – Premium Quality & Performance
    9. EN 12165 Grade CuZn40Pb2 H080 – Lead‑Added Copper Alloy for Enhanced Machinability
    10. EN 12165 Grade CuZn39Pb3 H080 – Lead-Enhanced Brass for Superior Machinability