ISO 683-1 Grade C22E Soft Annealed Steel – Ideal for Heavy Forged Parts & Vehicle Components

Steel C22E is suitable for low strained components of higher dimensions (heavy forged parts) and more complex forms as well as higher demands on uniformity of qualities and surface appearance in vehicle and machine engineering (e.g. transmission parts, crankshafts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

156 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

52 - 56.9 W/(m·K)

100.0 °C

51 - 56.4 W/(m·K)

200.0 °C

49 - 53.5 W/(m·K)

300.0 °C

46 - 49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.17 - 0.24 %

Chromium

0.4 %

Manganese

0.4 - 0.7 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. ISO 4957 Grade X32CrMoV3-3 Soft Annealed Steel (+A) – High-Performance Hot Working Alloy
    2. EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
    3. X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
    4. EN 10083-2 Grade C50R Soft Annealed Steel (+A) – High Strength & Workability
    5. EN 10083-2 Grade C55R Soft Annealed Steel – Enhanced Workability for Automotive and Engineering Applications
    6. EN 10269 Grade 40CrMoV4-6 Soft-Annealed Steel – Ideal for High‑Temperature Fasteners
    7. EN 10269 Grade 42CrMo4 Soft-Annealed Steel – High Strength & Wear Resistance
    8. ISO 683-2 Grade 36CrNiMo4 Soft-Annealed Steel (+A) – High-Performance Alloy for Heavy-Duty Applications
    9. ISO 683-1 Grade C22E – Normalized & Normalized Formed Steel for Heavy Forged Parts
    10. ISO 683-1 Grade C22E – High-Performance Quenched & Tempered Steel for Heavy-Duty Applications