EN 1652 Grade CuZn30 (G010) – Premium Unhardenable Copper Alloy

CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn30 is used for deep drawing components, musical instruments, hose tubes, springing elements, clockfaces and as cladding material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.5 - 8.55 g/cm³

Grain size

0.02 μm

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

114 GPa

100.0 °C

112 GPa

200.0 °C

107 GPa

300.0 °C

103 GPa

400.0 °C

96 GPa

500.0 °C

88 GPa

600.0 °C

77 GPa

700.0 °C

67 GPa

Elongation A50

20.0 °C

40 %

Hardness, Vickers

20.0 °C

120 [-]

Poisson's ratio

20.0 °C

0.34 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

410 MPa

Yield strength Rp0.2

20.0 °C

210 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.9E-5 1/K

150.0 °C

1.9E-5 1/K

300.0 °C

2E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

100.0 °C

398 J/(kg·K)

200.0 °C

410 J/(kg·K)

300.0 °C

419 J/(kg·K)

400.0 °C

431 J/(kg·K)

500.0 °C

444 J/(kg·K)

600.0 °C

452 J/(kg·K)

700.0 °C

456 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

121 - 126 W/(m·K)

200.0 °C

147 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.60E+7 S/m

Electrical resistivity

200.0 °C

7.7E-8 Ω·m

500.0 °C

1.08E-7 Ω·m

Specific Electrical conductivity

28 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Copper

69 - 71 %

Iron

0.05 %

Lead

0.05 %

Nickel

0.3 %

Phosphorus

0.2 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1652 CuZn30 H055 – Premium Unhardenable Copper Alloy for Precision Applications
    2. EN 1652 Grade CuZn30 H095 – High-Performance Copper Alloy for Advanced Applications
    3. EN 1652 Grade CuZn30 H120 – High-Strength Wrought Copper Alloy
    4. EN 1652 CuZn30 (CW505L) Wrought Alloy – High Strength, Excellent Workability
    5. EN 1652 CuZn30 R480 – High‑Strength, Unhardenable Copper Alloy for Deep Drawing & More
    6. EN 1652 Grade CuZn37 (G010) – Premium Unhardenable Wrought Copper Alloy
    7. EN 1652 Grade CuZn30 R270 – Premium Unhardenable Copper Alloy
    8. EN 1652 CuZn30 (CW505L) – High-Strength Unhardenable Wrought Copper Alloy for Precision Applications
    9. EN 1652 Grade CuZn30 (CW505L) – Premium Unhardenable Wrought Copper Alloy for High-Strength Applications
    10. EN 1652 CuZn30 G075: Premium Unhardenable Copper Alloy