EN 10250-4 X2CrNi19-11 Stainless Steel – Solution Annealed (+AT) – High Corrosion Resistance & Premium Quality

The make X2CrNi19-11, a modification of 1.4301, is comparable to X 2CrNi 19 11 acc. to DIN 17440 : 1985-07. Resistance to intercrystalline corrosion in delivery condition as well as in sensitized condition due to the lowered C-content. Application in chemical apparatus engineering and in pharmaceutical industry especially for requirement to high wall thickness and usability for mirror finishing, in nuclear reactor engineering, for parts in food industry exposed to organic or fruit acids, in oil, soap and synthetic fiber industry. Generally resistant up to pH-value 4,5 in aggressive media poor in chloride.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.92 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-269.0 °C

201.3 GPa

-195.0 °C

205.1 GPa

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

27.0 °C

190.2 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation, transverse

20.0 °C

35 %

Poisson's ratio

-269.0 °C

0.31 [-]

-195.0 °C

0.29 [-]

20.0 °C

0.29 [-]

27.0 °C

0.27 [-]

Shear modulus

20.0 °C

75.7 GPa

Tensile strength, transverse

20.0 °C

460 - 680 MPa

Yield strength Rp0.2

100.0 °C

147 MPa

150.0 °C

132 MPa

200.0 °C

118 MPa

250.0 °C

108 MPa

300.0 °C

100 MPa

350.0 °C

94 MPa

400.0 °C

89 MPa

450.0 °C

85 MPa

500.0 °C

81 MPa

550.0 °C

80 MPa

Yield strength Rp0.2, transverse

20.0 °C

180 MPa

Yield strength Rp1.0

100.0 °C

181 MPa

150.0 °C

162 MPa

200.0 °C

147 MPa

250.0 °C

137 MPa

300.0 °C

127 MPa

350.0 °C

121 MPa

400.0 °C

116 MPa

450.0 °C

112 MPa

500.0 °C

109 MPa

550.0 °C

108 MPa

Yield strength Rp1.0, transverse

20.0 °C

215 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

20.0 °C

13.9 - 15 W/(m·K)

100.0 °C

15.4 W/(m·K)

200.0 °C

17.2 W/(m·K)

300.0 °C

18.7 W/(m·K)

400.0 °C

20.2 W/(m·K)

500.0 °C

21.6 W/(m·K)

600.0 °C

23 W/(m·K)

700.0 °C

24.4 W/(m·K)

800.0 °C

25.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.7 mm²/s

100.0 °C

3.9 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.5 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.35E-7 Ω·m

100.0 °C

8E-7 Ω·m

200.0 °C

8.68E-7 Ω·m

300.0 °C

9.33E-7 Ω·m

400.0 °C

9.89E-7 Ω·m

500.0 °C

1.04E-6 Ω·m

600.0 °C

1.08E-6 Ω·m

700.0 °C

1.12E-6 Ω·m

800.0 °C

1.15E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

18 - 20 %

Manganese

2 %

Nickel

10 - 12 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-4 Grade X2CrNiMoCuN25-6-3 – Solution Annealed Steel for High-Performance Applications
    2. EN 10250-4 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed for High-Performance Applications
    3. EN 10250-4 Grade X2CrNiMoN25-7-4: Solution-Annealed Steel for High-Performance Applications
    4. EN 10250-4 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Stainless Steel for High-Performance Applications
    5. EN 10250-4 X2CrNi18-9 Austenitic Steel – Solution Annealed + AT
    6. EN 10250-4 X2CrNiN23-4 Duplex Stainless Steel – Solution Annealed (+AT)
    7. EN 10250-4 Grade X3CrNiMoN27-5-2 Solution Annealed – High-Performance Stainless Steel for Corrosion Resistance
    8. EN 10250-4 Grade X2CrNiMo17-12-2 Solution-Annealed Steel (+AT) – High Corrosion Resistance
    9. EN 10250-4 X2CrNiMoN17-11-2 Solution-Annealed Steel for High-Performance Chemical Applications
    10. EN 10250-4 X2CrNiMoN17-13-3 Steel – Solution Annealed, Enhanced Corrosion Resistance