The make X2CrNIMo17-12-2 is comparable to X 2 CrNiMo 17 13 2 acc. to DIN17440 : 1985-07. It is a modification of steel 1.4401 and a steel of high resistance to non-oxidizing acids and chloride-containing media. The steel is usable for mirror finishing and cold forming. Improved corrosion properties due to the lowered C-content. The material is resistant to intercrystalline corrosion also in sensitized condition. Application in apparatus engineering of chemical industry as well as in cellulose, textile and pharmaceutical industry and in sewage plants.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength, transverse

20.0 °C

500 - 700 MPa

Yield strength Rp0.2

100.0 °C

166 MPa

150.0 °C

152 MPa

200.0 °C

137 MPa

250.0 °C

127 MPa

300.0 °C

118 MPa

350.0 °C

113 MPa

400.0 °C

108 MPa

450.0 °C

103 MPa

500.0 °C

100 MPa

550.0 °C

98 MPa

Yield strength Rp0.2, transverse

20.0 °C

200 MPa

Yield strength Rp1.0

100.0 °C

199 MPa

150.0 °C

181 MPa

200.0 °C

167 MPa

250.0 °C

157 MPa

300.0 °C

145 MPa

350.0 °C

139 MPa

400.0 °C

135 MPa

450.0 °C

130 MPa

500.0 °C

128 MPa

550.0 °C

127 MPa

Yield strength Rp1.0, transverse

20.0 °C

235 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10 - 13 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-4 Grade X2CrNiMoCuN25-6-3 – Solution Annealed Steel for High-Performance Applications
    2. EN 10250-4 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed for High-Performance Applications
    3. EN 10250-4 Grade X2CrNiMoN25-7-4: Solution-Annealed Steel for High-Performance Applications
    4. EN 10269 X2CrNiMo17-12-2 Solution-Annealed Steel – Superior Corrosion Resistance & Formability
    5. EN 10250-4 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Stainless Steel for High-Performance Applications
    6. EN 10250-4 X2CrNi18-9 Austenitic Steel – Solution Annealed + AT
    7. EN 10250-4 X2CrNiN23-4 Duplex Stainless Steel – Solution Annealed (+AT)
    8. EN 10250-4 Grade X3CrNiMoN27-5-2 Solution Annealed – High-Performance Stainless Steel for Corrosion Resistance
    9. EN 10222-5 Grade X2CrNiMo17-12-2 – Solution Annealed Steel for High-Performance Corrosion Resistance
    10. EN 10250-4 X2CrNi19-11 Stainless Steel – Solution Annealed (+AT) – High Corrosion Resistance & Premium Quality