EN 10222-5 Grade X2CrNiMo17-12-2 – Solution Annealed Steel for High-Performance Corrosion Resistance

Trademark X2CrNiMo17-12-2 is a modification of steel 1.4401. To the comparable DIN-make X 2 CrNiMo 17 13 2 acc. to DIN 17440 : 1985-07 applies: The material shows high resistance to non-oxidizing acids and chloride-containing media. It is suitable for mirror finishing and very well cold formable. Its corrosion properties are still improved due to the lowered C-content. This material is resistant to intercrystalline corrosion also in sensitized condition. Application in chemical apparatus engineering as well as in cellulose, textile and pharmaceutical industry and in sewage plants. It is approved for pressure vessel construction up to 400 °C., beyond it subject to authorization.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 - 45 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

490 - 690 MPa

Yield strength Rp0.2

20.0 °C

190 MPa

Yield strength Rp1.0

20.0 °C

225 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

0 - 400 °C

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10 - 13 %

Nitrogen

0.1 - 0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10222-5 X2CrNi18-9 Solution-Annealed Steel (+AT) – High Corrosion & Mechanical Strength
    2. EN 10222-5 Grade X2CrNiCu19-10 – Solution Annealed Stainless Steel (AT)
    3. EN 10222-5 Grade X2CrNiMo17-12-3: Solution Annealed + AT – Premium Austenitic Steel
    4. EN 10222-5 X3CrNiMo18-12-3 – Solution Annealed Stainless Steel, Ideal for Pressure Vessels
    5. EN 10222-5 Grade X7CrNiNb18-10 – Solution-Annealed Stainless Steel for Corrosion‑Resistant Pressure Vessels
    6. EN 10222‑5 X6CrNiTiB18‑10 Solution‑Annealed Steel for High‑Temperature Applications
    7. EN 10269 X2CrNiMo17-12-2 Solution-Annealed Steel – Superior Corrosion Resistance & Formability
    8. EN 10222-5 Grade X2CrNiMoN17-11-2 – Solution Annealed Steel with Enhanced Corrosion Resistance
    9. EN 10222-5 X5CrNiMo17-12-2: Solution-Annealed Austenitic Steel for Chemical & Pharmaceutical Use
    10. EN 10222-5 Grade X6CrNi18-10 (Solution Annealed + AT): High‑Temperature Austenitic Steel for Reactor, Boiler, and Chemical Applications