EN 10250‑4 X1NiCrMoCu25‑20‑5 Solution‑Annealed Steel (+AT) – High‑Performance Corrosion‑Resistant Alloy

The make X1NiCrMoCu25-20-5 is comparable to X 1 NiCrMoCuN 25 20 5 acc. to SEW 400 : 1991-02. The material is an austenitic steel of high resistance to highly aggressive organic and inorganic acids, high pitting and largely stress corosion resistance. Interaction parameter 39 (second best pitting index of all steels). The material is resistant to intercrystalline corrosion also in welded condition. Application in chemical and petrochemical industry, for flue gas desulfurizing plants, in cellulose and paper industry as well as for smokestack lining.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.76 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

195 - 196 GPa

100.0 °C

190 GPa

200.0 °C

182 GPa

300.0 °C

174 GPa

400.0 °C

166 GPa

500.0 °C

158 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength, transverse

20.0 °C

530 - 730 MPa

Yield strength Rp0.2

100.0 °C

205 MPa

150.0 °C

190 MPa

200.0 °C

175 MPa

250.0 °C

160 MPa

300.0 °C

145 MPa

350.0 °C

135 MPa

400.0 °C

125 MPa

450.0 °C

115 MPa

500.0 °C

110 MPa

550.0 °C

105 MPa

Yield strength Rp0.2, transverse

20.0 °C

230 MPa

Yield strength Rp1.0

100.0 °C

235 MPa

150.0 °C

220 MPa

200.0 °C

205 MPa

250.0 °C

190 MPa

300.0 °C

175 MPa

350.0 °C

165 MPa

400.0 °C

155 MPa

450.0 °C

145 MPa

500.0 °C

140 MPa

550.0 °C

135 MPa

Yield strength Rp1.0, transverse

20.0 °C

260 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.58E-5 - 1.67E-5 1/K

200.0 °C

1.61E-5 - 1.72E-5 1/K

300.0 °C

1.65E-5 - 1.77E-5 1/K

400.0 °C

1.69E-5 - 1.81E-5 1/K

500.0 °C

1.73E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

450 - 472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

11.9 - 12 W/(m·K)

100.0 °C

13.3 W/(m·K)

200.0 °C

15.1 W/(m·K)

300.0 °C

16.7 W/(m·K)

400.0 °C

18.3 W/(m·K)

500.0 °C

19.8 W/(m·K)

600.0 °C

21.3 W/(m·K)

700.0 °C

22.8 W/(m·K)

800.0 °C

24.3 W/(m·K)

900.0 °C

25.7 W/(m·K)

1000.0 °C

27.1 W/(m·K)

Thermal diffusivity

20.0 °C

3.3 mm²/s

100.0 °C

3.4 mm²/s

200.0 °C

3.7 mm²/s

300.0 °C

4.1 mm²/s

400.0 °C

4.3 mm²/s

500.0 °C

4.5 mm²/s

600.0 °C

4.7 mm²/s

700.0 °C

5 mm²/s

800.0 °C

5.4 mm²/s

900.0 °C

5.7 mm²/s

1000.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

9.59E-7 Ω·m

100.0 °C

1.01E-6 Ω·m

200.0 °C

1.05E-6 Ω·m

300.0 °C

1.1E-6 Ω·m

400.0 °C

1.13E-6 Ω·m

500.0 °C

1.17E-6 Ω·m

600.0 °C

1.19E-6 Ω·m

700.0 °C

1.22E-6 Ω·m

800.0 °C

1.24E-6 Ω·m

900.0 °C

1.26E-6 Ω·m

1000.0 °C

1.28E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.02 %

Chromium

19 - 21 %

Copper

1.2 - 2 %

Manganese

2 %

Molybdenum

4 - 5 %

Nickel

24 - 26 %

Nitrogen

0.15 %

Phosphorus

0.03 %

Silicon

0.7 %

Sulfur

0.01 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-4 Grade X2CrNiMoCuN25-6-3 – Solution Annealed Steel for High-Performance Applications
    2. EN 10250-4 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed for High-Performance Applications
    3. EN 10250-4 Grade X2CrNiMoN25-7-4: Solution-Annealed Steel for High-Performance Applications
    4. EN 10250-4 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Stainless Steel for High-Performance Applications
    5. EN 10250-4 X2CrNi18-9 Austenitic Steel – Solution Annealed + AT
    6. EN 10250-4 X2CrNiN23-4 Duplex Stainless Steel – Solution Annealed (+AT)
    7. EN 10250-4 Grade X3CrNiMoN27-5-2 Solution Annealed – High-Performance Stainless Steel for Corrosion Resistance
    8. EN 10250-4 X2CrNi19-11 Stainless Steel – Solution Annealed (+AT) – High Corrosion Resistance & Premium Quality
    9. EN 10250-4 Grade X2CrNiMo17-12-2 Solution-Annealed Steel (+AT) – High Corrosion Resistance
    10. EN 10250-4 X2CrNiMoN17-11-2 Solution-Annealed Steel for High-Performance Chemical Applications