EN 10277‑5 Grade C45 Steel – Cold‑Drawn, Turned, Quenched & Tempered

Steel C 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering (e.g. transmission shafts, gear wheels, transmission parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210.11 - 212 GPa

100.0 °C

205.02 - 207 GPa

200.0 °C

198.84 - 199 GPa

300.0 °C

191.42 - 192 GPa

400.0 °C

183.23 - 184 GPa

500.0 °C

173.19 - 175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

14 - 17 %

Poisson's ratio

20.0 °C

0.28 [-]

100.0 °C

0.28 [-]

200.0 °C

0.29 [-]

300.0 °C

0.29 [-]

400.0 °C

0.3 [-]

500.0 °C

0.3 [-]

Reduction of area

20.0 °C

35 - 45 %

Shear modulus

20.0 °C

82.04 GPa

100.0 °C

80.03 GPa

200.0 °C

77.09 GPa

300.0 °C

74.16 GPa

400.0 °C

70.76 GPa

500.0 °C

66.74 GPa

Tensile strength

20.0 °C

630 - 850 MPa

Yield strength

20.0 °C

370 - 490 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 480 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.42 - 0.5 %

Manganese

0.5 - 0.8 %

Phosphorus

0.05 %

Silicon

0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. High-Strength 25CrMo4 Steel – EN 10277-5 Cold-Drawn, Turned, Quenched & Tempered
    2. EN 10277‑5: 25CrMoS4 Cold‑Drawn, Quenched & Tempered – Premium High‑Strength Steel for Automotive & Engine Parts
    3. EN 10277-5 Grade 28Cr4: High‑Strength Cold Drawn or Turned Steel, Quenched and Tempered
    4. EN 10277-5 Grade 34CrS4 Cold-Drawn or Turned Steel – Quenched & Tempered for Vehicle and Engine Applications
    5. EN 10277-5 Grade 36CrNiMo4 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Performance Applications
    6. EN 10277-5 Grade 37Cr4: Premium Cold-Drawn & Quenched Steel for High-Performance Automotive & Machine Parts
    7. EN 10277-5 Grade 37CrS4: High-Performance Cold-Drawn, Quenched, and Tempered Steel for Automotive & Machinery Applications
    8. EN 10277-5 Grade 38Cr2 – Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Automotive Components
    9. EN 10277-5 Grade 38CrS2: High-Strength Cold-Drawn, Turned, Quenched & Tempered Steel
    10. EN 10277‑5 Grade C45 Steel – Cold‑Drawn, Turned, Quenched & Tempered