EN 10277-2 Grade C16 Cold-Drawn Bar Steel – High Strength & Precision
As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 7 - 12 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 360 - 820 MPa | |
Yield strength Rp0.2 | 20.0 °C | 235 - 400 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.12 - 0.18 % |
Manganese | 0.6 - 0.9 % |
Phosphorus | 0.05 % |
Silicon | 0.4 % |
Sulfur | 0.045 % |
Metal
- EN 10277-2 Grade E295GC Cold Drawn Steel – High Strength & Wear Resistance
- EN 10277‑2 Grade E335GC Cold Drawn Steel – High Strength & Wear Resistance
- EN 10277-2 Grade ZSt50-2: Premium Cold-Drawn Steel for High-Performance Applications
- EN 10277‑2 Grade ZSt60‑2: Premium Cold‑Drawn Steel for High‑Wear, High‑Strength Applications
- EN 10277-2 Grade ZSt70-2: Premium Cold-Drawn High-Carbon Steel for Wear-Resistant Components
- EN 10277-2 Grade C35 Cold-Drawn Steel – High Strength, Low Temperature Performance
- EN 10277-2 Grade C40 Cold Drawn Steel – High Strength for Vehicle & Machine Engineering
- EN 10277-2 Grade C45 Cold Drawn Steel – High-Performance Structural Material
- EN 10277-2 Grade C50 Cold Drawn Steel – High Strength & Wear Resistance
- EN 10277-2 Grade C60 Cold-Drawn Steel – High Strength & Wear Resistance