EN 10089 Grade 61SiCr7 Steel – Quenched & Tempered for High-Performance Springs

The steel 61SiCr7 is used for formed springs, like leaf springs from 7 mm thickness for the vehicle construction as well as for leaf and diaphragm springs (also for the mechanical engineering).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

206 - 207 GPa

200.0 °C

199 - 200 GPa

300.0 °C

192 - 193 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

5.5 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

20 %

Shear modulus

20.0 °C

80 GPa

Tensile strength

20.0 °C

1550 - 1850 MPa

Yield strength Rp0.2

20.0 °C

1400 MPa

Thermal

PropertyTemperatureValue

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.57 - 0.65 %

Chromium

0.2 - 0.45 %

Manganese

0.7 - 1 %

Phosphorus

0.03 %

Silicon

1.6 - 2 %

Sulfur

0.025 %

Technological properties

Property
Features

Spring


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
    3. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    4. EN 10089 60Cr3 Quenched & Tempered Steel – Ideal for Springs & Mechanical Applications
    5. EN 10089 Grade 60CrMo3-1 Quenched & Tempered Steel – High-Performance Spring Material
    6. EN 10089 Grade 60CrMo3-2: Quenched & Tempered (QT) Steel for High-Performance Vehicle Springs
    7. EN 10089 Grade 60CrMo3-3 Quenched & Tempered Steel for High‑Performance Springs
    8. EN 10089 Grade 38Si7 Quenched & Tempered Steel – Ideal for Springs & Load‑Securing Applications
    9. EN 10089 Grade 51CrV4 Quenched & Tempered Steel – Premium for High‑Temperature Springs
    10. EN 10089 Grade 52CrMoV4 (QT) – High-Strength Steel for Vehicle Springs