DIN 17111 Grade U10S10 Hot-Rolled Steel – Ideal for Fasteners

The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

340 - 470 MPa

Yield strength

20.0 °C

215 - 225 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

57.5 W/(m·K)

100.0 °C

55.7 W/(m·K)

200.0 °C

51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.15 %

Manganese

0.3 - 0.6 %

Phosphorus

0.05 %

Sulfur

0.08 - 0.12 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17111 Grade R10S10 Hot Rolled Steel – Ideal for Bolts, Nuts & Rivets
    2. DIN 17111 Grade R7S6 Hot-Rolled Steel – Ideal for Fasteners
    3. DIN 488-1 Grade BSt 500 G Hot Rolled Rebar Wire – High Strength, Smooth Finish
    4. DIN 17111 Grade U 7 S 6 Hot Rolled Steel – Ideal for Fasteners
    5. DIN 17111 RSt 38 Hot Rolled Steel – Ideal for Fasteners
    6. DIN 17111 Grade UQSt 36 Hot Rolled Steel – Ideal for Cold Heading and Fastener Production
    7. DIN 17111 Grade UQSt 38 Hot Rolled Steel – Ideal for Cold Heading & Fastener Production
    8. DIN 17111 Grade USt 36 Hot Rolled Steel – High-Quality Material for Fasteners
    9. DIN 17111 Grade USt 38 Hot-Rolled Steel – Ideal for Bolts, Nuts & Rivets
    10. DIN 17111 RSt 36 Hot-Rolled Steel – Ideal for Bolts, Nuts, and Rivets