DIN 17111 Grade UQSt 36 Hot Rolled Steel – Ideal for Cold Heading and Fastener Production

The steel is suitable for cold heading and is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

330 - 430 MPa

Yield strength

20.0 °C

195 - 205 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.14 %

Manganese

0.25 - 0.5 %

Phosphorus

0.04 %

Sulfur

0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17111 Grade R10S10 Hot Rolled Steel – Ideal for Bolts, Nuts & Rivets
    2. DIN 17111 Grade R7S6 Hot-Rolled Steel – Ideal for Fasteners
    3. DIN 488-1 Grade BSt 500 G Hot Rolled Rebar Wire – High Strength, Smooth Finish
    4. DIN 17111 Grade U10S10 Hot-Rolled Steel – Ideal for Fasteners
    5. DIN 17111 Grade U 7 S 6 Hot Rolled Steel – Ideal for Fasteners
    6. DIN 17111 RSt 38 Hot Rolled Steel – Ideal for Fasteners
    7. DIN 17111 Grade UQSt 38 Hot Rolled Steel – Ideal for Cold Heading & Fastener Production
    8. DIN 17111 Grade USt 36 Hot Rolled Steel – High-Quality Material for Fasteners
    9. DIN 17111 Grade USt 38 Hot-Rolled Steel – Ideal for Bolts, Nuts & Rivets
    10. DIN 17111 RSt 36 Hot-Rolled Steel – Ideal for Bolts, Nuts, and Rivets