EN 10217-7 Grade X2CrNiMoN17-13-5 – Solution Annealed Stainless Steel for High-Temperature Corrosion Resistance

The austenitic steel X2CrNiMoN17-13-5 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 - 8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

20.0 °C

580 - 800 MPa

Tensile strength, transverse

20.0 °C

580 - 800 MPa

Yield strength Rp0.2

20.0 °C

285 MPa

50.0 °C

260 MPa

100.0 °C

225 MPa

150.0 °C

200 MPa

200.0 °C

185 MPa

250.0 °C

175 MPa

300.0 °C

165 MPa

350.0 °C

155 MPa

400.0 °C

150 MPa

Yield strength Rp0.2, transverse

20.0 °C

285 MPa

Yield strength Rp1.0

20.0 °C

315 MPa

50.0 °C

290 MPa

100.0 °C

255 MPa

150.0 °C

230 MPa

200.0 °C

210 MPa

250.0 °C

200 MPa

300.0 °C

190 MPa

350.0 °C

180 MPa

400.0 °C

175 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 - 14 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.75E-7 - 8.5E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

4 - 5 %

Nickel

12.5 - 14.5 %

Nitrogen

0.12 - 0.22 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10217-7 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed Steel for Corrosion‑Resistant Tubes
    2. EN 10217-7 Grade X2CrNiMoN25-7-4 Solution-Annealed Steel (+AT) – High-Temperature Corrosion Resistance
    3. EN 10217-7 X2CrNiN23-4 Austenitic Ferritic Steel – Solution Annealed for Corrosion-Resistant Tubes
    4. EN 10217-7 Grade X1NiCrMoCuN25-20-7 – Solution‑Annealed Stainless Steel for High‑Temperature Corrosion Resistance
    5. EN 10217-7 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Steel for High-Performance Applications
    6. EN 10217-7 X2CrNi18-9 Solution-Annealed Austenitic Steel – High-Performance Tubing
    7. EN 10217-7 Grade X2CrNiMoN22-5-3 Solution‑Annealed Steel (+AT) – High‑Performance, Corrosion‑Resistant Tubing
    8. EN 10217‑7 Grade X2CrNiMoN17‑13‑3 – Solution Annealed Steel for Corrosion‑Resistant, High‑Temperature Applications
    9. EN 10217-7 Grade X2CrNiN18-10: Solution-Annealed Stainless Steel for High-Performance Applications
    10. EN 10217-7 Grade X3CrNiMo17-13-3 – Solution Annealed (AT) – High-Performance Austenitic Steel