EN 10217-7 X5CrNi18-10 Austenitic Steel – Solution Annealed (+AT) for Corrosion Resistance

The austenitic steel X5CrNi18-10 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 300 °C) also in the welded condition.

Additional services: To ensure our customers' processes and/or products attain – and even exceed – their performance expectations, we offer a wide range of services within both the technical area and delivery logistics. Our technical services include: • Material consultations through our worldwide sales network • Advice in process optimization based on an in-depth applications knowledge • Joint new product development supported by our extensive R&D program View product groups and services

UGITECH

MANUFACTURER

Information and services

Additional services: https://eservices.ugitech.com/

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.92 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

24.0 °C

194.4 - 196.5 GPa

100.0 °C

190 - 194 GPa

149.0 °C

188.2 - 189.6 GPa

200.0 °C

182 - 186 GPa

260.0 °C

182.7 - 184.1 GPa

300.0 °C

174 - 179 GPa

371.0 °C

173.1 - 177.9 GPa

400.0 °C

166 - 172 GPa

483.0 °C

157.9 - 160 GPa

500.0 °C

158 - 165 GPa

593.0 °C

149.6 - 155.8 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

704.0 °C

137.9 - 144.8 GPa

800.0 °C

134 GPa

816.0 °C

120.7 - 128.2 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

35 %

Poisson's ratio

20.0 °C

0.28 [-]

24.0 °C

0.24 - 0.25 [-]

149.0 °C

0.27 - 0.3 [-]

260.0 °C

0.29 - 0.32 [-]

371.0 °C

0.32 [-]

483.0 °C

0.27 - 0.29 [-]

593.0 °C

0.29 - 0.3 [-]

704.0 °C

0.27 - 0.3 [-]

816.0 °C

0.23 - 0.27 [-]

Shear modulus

24.0 °C

78.6 GPa

149.0 °C

72.4 - 74.5 GPa

260.0 °C

69.6 - 71 GPa

371.0 °C

65.5 - 67.6 GPa

483.0 °C

62.1 GPa

593.0 °C

57.9 - 60 GPa

704.0 °C

54.5 - 55.9 GPa

816.0 °C

49 - 50.3 GPa

Tensile strength

20.0 °C

500 - 700 MPa

Tensile strength, transverse

20.0 °C

500 - 700 MPa

Yield strength Rp0.2

20.0 °C

195 MPa

50.0 °C

180 MPa

100.0 °C

155 MPa

150.0 °C

140 MPa

200.0 °C

127 MPa

250.0 °C

118 MPa

300.0 °C

110 MPa

350.0 °C

104 MPa

400.0 °C

98 MPa

450.0 °C

95 MPa

500.0 °C

92 MPa

550.0 °C

90 MPa

Yield strength Rp0.2, transverse

20.0 °C

195 MPa

Yield strength Rp1.0

20.0 °C

230 MPa

50.0 °C

218 MPa

100.0 °C

190 MPa

150.0 °C

170 MPa

200.0 °C

155 MPa

250.0 °C

145 MPa

300.0 °C

135 MPa

350.0 °C

129 MPa

400.0 °C

125 MPa

450.0 °C

122 MPa

500.0 °C

120 MPa

550.0 °C

120 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

-100.0 °C

11.7 W/(m·K)

20.0 °C

14.5 - 15 W/(m·K)

100.0 °C

16 W/(m·K)

200.0 °C

17.6 W/(m·K)

300.0 °C

19.1 W/(m·K)

400.0 °C

20.4 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.7 W/(m·K)

800.0 °C

26.1 W/(m·K)

Thermal diffusivity

-100.0 °C

3.7 mm²/s

20.0 °C

3.9 mm²/s

100.0 °C

4.3 mm²/s

200.0 °C

4.3 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

5.86E-7 Ω·m

20.0 °C

6.92E-7 - 7.3E-7 Ω·m

100.0 °C

7.58E-7 Ω·m

200.0 °C

8.36E-7 Ω·m

300.0 °C

9.07E-7 Ω·m

400.0 °C

9.73E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.06E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.13E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.07 %

Chromium

17 - 19.5 %

Manganese

2 %

Nickel

8 - 10.5 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10222-5 X2CrNiMo18-14-3 Solution‑Annealed Grade for Corrosion‑Resistant Applications
    2. EN 10269 X5CrNi18-10 Austenitic Stainless Steel – Solution Annealed with Annealing Treatment
    3. EN 10222‑5 X5CrNi18‑10 Solution Annealed (+AT): High‑Performance Austenitic Stainless Steel
    4. EN 10250-4 Grade X5CrNi18-10 Solution-Annealed Steel (+AT) – Premium Corrosion-Resistant Austenitic Alloy
    5. EN 10217-7 Grade X6CrNiMoTi17-12-2 Solution-Annealed Steel – High‑Temperature Corrosion Resistance & Structural Strength
    6. EN 10217-7 X6CrNiTi18-10 Solution-Annealed Austenitic Steel – Corrosion-Resistant & High-Temperature Performance
    7. X2CrNiMo18-14-3 Austenitic Steel – Solution Annealed (EN 10217‑7) – Superior Corrosion & Temperature Resistance
    8. EN 10216-5 Grade X5CrNi18-10 Solution Annealed (+AT) – High Corrosion Resistance Stainless Steel
    9. EN 10272 Grade X5CrNi18-10 Solution-Annealed Steel (+AT): Premium Austenitic Steel for Pressure Vessels
    10. EN 10028-7 Grade X5CrNi18-10 Solution Annealed (+AT) – High-Performance Austenitic Stainless Steel