EN 10272 X6CrNiMoTi17-12-2 Steel – Solution-Annealed, High‑Performance Corrosion Resistance

Steel grade X6CrNiMoTi17-12-2 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. the material is the stabilized by Ti option of 1.4401. The steel shows increased corrosion resistance to non-oxidizing acids and halogenated media due to the high Mo-content. It has increased resistance to intercrystaliine corrosion due to the Ti-content, also in sensitized condition. The material is unsuitable for mirror finishing.

Additional services: To ensure our customers' processes and/or products attain – and even exceed – their performance expectations, we offer a wide range of services within both the technical area and delivery logistics. Our technical services include: • Material consultations through our worldwide sales network • Advice in process optimization based on an in-depth applications knowledge • Joint new product development supported by our extensive R&D program View product groups and services

UGITECH

MANUFACTURER

Information and services

Additional services: https://eservices.ugitech.com/

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

30 %

Hardness, Brinell

20.0 °C

215 [-]

Hardness, Brinell, trans

20.0 °C

215 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

500 - 700 MPa

100.0 °C

440 MPa

150.0 °C

410 MPa

200.0 °C

390 MPa

250.0 °C

385 MPa

300.0 °C

375 MPa

350.0 °C

375 MPa

400.0 °C

375 MPa

450.0 °C

370 MPa

500.0 °C

360 MPa

550.0 °C

330 MPa

Tensile strength, transverse

20.0 °C

500 - 700 MPa

Yield strength Rp0.2

20.0 °C

200 MPa

100.0 °C

185 MPa

150.0 °C

175 MPa

200.0 °C

165 MPa

250.0 °C

155 MPa

300.0 °C

145 MPa

350.0 °C

140 MPa

400.0 °C

135 MPa

450.0 °C

131 MPa

500.0 °C

129 MPa

550.0 °C

127 MPa

Yield strength Rp0.2, transverse

20.0 °C

200 MPa

Yield strength Rp1.0

20.0 °C

235 MPa

100.0 °C

215 MPa

150.0 °C

205 MPa

200.0 °C

192 MPa

250.0 °C

183 MPa

300.0 °C

175 MPa

350.0 °C

169 MPa

400.0 °C

164 MPa

450.0 °C

160 MPa

500.0 °C

158 MPa

550.0 °C

157 MPa

Yield strength Rp1.0, transverse

20.0 °C

235 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.65E-5 - 1.67E-5 1/K

200.0 °C

1.72E-5 - 1.75E-5 1/K

300.0 °C

1.77E-5 - 1.8E-5 1/K

400.0 °C

1.81E-5 - 1.85E-5 1/K

500.0 °C

1.84E-5 - 1.9E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10.5 - 13.5 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 - 0.03 %

Titanium

0.7 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10222-5 X2CrNiMo18-14-3 Solution‑Annealed Grade for Corrosion‑Resistant Applications
    2. EN 10222-5 X6CrNiMoTi17-12-2 (Solution Annealed) – High Corrosion‑Resistant Stainless Steel
    3. EN 10222-5 X6CrNiTi18-10 – Solution Annealed & AT: Premium Corrosion‑Resistant Steel for Chemical & Food Applications
    4. X2CrNiMo18-14-3 Solution Annealed – EN 10250-4 Grade, Superior Corrosion Resistance
    5. EN 10250-4 X6CrNiMoTi17-12-2 (Solution Annealed) – High-Performance Stainless Steel
    6. EN 10217-7 Grade X6CrNiMoTi17-12-2 Solution-Annealed Steel – High‑Temperature Corrosion Resistance & Structural Strength
    7. EN 10216‑5 X6CrNiMoTi17‑12‑2: Solution‑Annealed Stainless Steel with Enhanced Corrosion Resistance
    8. X2CrNiMo18-14-3 Grade Steel – Solution Annealed with AT – EN 10272 Standard
    9. EN 10272 Grade X5CrNi18-10 Solution-Annealed Steel (+AT): Premium Austenitic Steel for Pressure Vessels
    10. EN 10272 X6CrNiMoTi17-12-2 Steel – Solution-Annealed, High‑Performance Corrosion Resistance