Alloy 165 (C17000) TD04 Rod & Bar – High Strength & Corrosion Resistance
Alloy 165 rod and bar from Materion Performance Alloys provide strength close to that of Alloy 25, with slightly lower beryllium content. This alloy features high fatigue strength, good electrical and thermal conductivity, as well as resistance to wear, corrosion, galling, and stress relaxation.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.41 g/cm³ |
Dimension
| Property | Value | Comment |
|---|---|---|
Diameter | 0.76 - 76 mm | |
Length | 91000 mm | max. |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 131 GPa |
Elongation | 23.0 °C | 8 - 30 % |
Tensile strength | 23.0 °C | 590 - 900 MPa |
Yield strength Rp0.2 | 23.0 °C | 520 - 720 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K |
Melting point | 870 °C | |
Thermal conductivity | 23.0 °C | 105 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 5.8E-6 - 6.9E-6 Ω·m |
Specific Electrical conductivity | 25 - 30 % IACS |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Beryllium | 1.6 - 1.85 % | ||
Cobalt | 0.2 % | min. Nickel + Cobalt | |
Copper | Balance | ||
Iron | 0.6 % | max., Nickel + Cobalt + Iron | |
Nickel | 0.2 % | min. Nickel + Cobalt | |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include bushings, bearings and resistance welding components. | |
Metal
- Alloy 25 Rod & Bar TD04 (C17200) – Premium Strength Copper Alloy
- Alloy 165 (C17000) TB00 Rods & Bars – High Strength, Low Beryllium, Industrial-Grade Performance
- High-Performance Alloy 165 (C17000) TF00 Rods & Bars – Superior Strength & Conductivity
- Alloy 165 (C17000) TH04 Rod & Bar – Superior Strength & Durability
- Alloy 3 (C17510) – High-Performance TB00 Rods & Bars
- High-Performance Alloy 3 (C17510) TD04 Rods and Bars – Superior Conductivity & Strength
- Alloy 3 (C17510) – Premium High-Conductivity Rod & Bar
- High-Conductivity Alloy 10 (C17500) TD04 Rods and Bars – Performance & Strength
- Alloy 165 (C17000) TD04 Plate – High‑Strength, Wear‑Resistant Performance Alloy
- Alloy 165 (C17000) TD04 Tube – High Fatigue Strength & Low Beryllium for Peak Performance