High-Performance Alloy 165 (C17000) TF00 Rods & Bars – Superior Strength & Conductivity
Alloy 165 rod and bar from Materion Performance Alloys provide strength close to that of Alloy 25, with slightly lower beryllium content. This alloy features high fatigue strength, good electrical and thermal conductivity, as well as resistance to wear, corrosion, galling, and stress relaxation.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.41 g/cm³ |
Dimension
| Property | Value | Comment |
|---|---|---|
Diameter | 0.76 - 356 mm | |
Length | 91000 mm | max. |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 131 GPa |
Elongation | 23.0 °C | 3 - 10 % |
Tensile strength | 23.0 °C | 1030 - 1310 MPa |
Yield strength Rp0.2 | 23.0 °C | 860 - 1070 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K |
Melting point | 870 °C | |
Thermal conductivity | 23.0 °C | 105 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 5.8E-6 - 6.9E-6 Ω·m |
Specific Electrical conductivity | 25 - 30 % IACS |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Beryllium | 1.6 - 1.85 % | ||
Cobalt | 0.2 % | min. Nickel + Cobalt | |
Copper | Balance | ||
Iron | 0.6 % | max., Nickel + Cobalt + Iron | |
Nickel | 0.2 % | min. Nickel + Cobalt | |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include bushings, bearings and resistance welding components. | |
Metal
- Alloy 165 Forging & Extrusion (TF00/C17000) – High Strength & Fatigue Resistance
- High-Strength Alloy 25 Rods & Bars – Superior Conductivity & Durability (C17200)
- Alloy 165 (C17000) TB00 Rods & Bars – High Strength, Low Beryllium, Industrial-Grade Performance
- Alloy 165 (C17000) TD04 Rod & Bar – High Strength & Corrosion Resistance
- Alloy 165 (C17000) TH04 Rod & Bar – Superior Strength & Durability
- Alloy 3 (C17510) – High-Performance TB00 Rods & Bars
- Alloy 3 (C17510) – Premium High-Conductivity Rod & Bar
- Alloy 10 (C17500) TF00 Rods & Bars – High Conductivity, Moderate Strength
- Alloy 165 (C17000) TF00 Plate – High-Performance, Corrosion-Resistant Steel for Demanding Applications
- Alloy 165 (C17000) TF00 Tube – High Strength, Low Beryllium, Near‑Unity Magnetic Permeability