DIN 5512-2 Grade St 37-2 G – Premium Cold‑Rolled Carbon Steel for Construction

St 37-2 G, material number 1.0037 according to DIN 1623/2, is a carbon construction steel, cold-rolled for general use. The material suitable for construction parts with simple forming, beveling, etc. It is used as a carrier material for galvanically refined strips and sheets. The steel is used as a carrier material for: - electrolytically refined strips and sheets: manufacturer/product: Thyssen:St 37-2 G ZE Voest-Alpine:Gravigal Zn, ZnNi

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

360 - 460 MPa

Yield strength

20.0 °C

215 - 315 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

0 - 1280 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.17 %

Nitrogen

7E-3 %

Phosphorus

0.04 %

Sulfur

0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. X5CrNiMoTi15-2 Cold-Rolled Steel (DIN 5512-3) – Durable Rail Vehicle Grade
    2. DIN 5512-2 St14 Steel Grade: Key Properties & Applications
    3. DIN 17222: Grade 55Si7 Cold‑Rolled & Hardened Steel – Precision Spring Material
    4. DIN 17222 Grade 71Si7: Premium Cold‑Rolled & Hardened Steel for High‑Load Tension Springs
    5. DIN 17222 Grade 50CrV4: Precision Cold‑Rolled & Hardened Steel for Springs
    6. DIN 17222 Grade 67SiCr5 Cold-Rolled & Hardened Steel for Precision Springs
    7. DIN 17222 Grade C55 Cold-Rolled & Hardened Steel – Precision Springs
    8. DIN 17222 C60 Cold-Rolled & Hardened Steel – Premium Spring Strip Grade
    9. DIN 1623 St 37‑3 G Cold‑Rolled Steel – Premium Construction Grade
    10. DIN 1623 St 44-3 G Cold‑Rolled Carbon Steel – Ideal for Construction Parts