EN 10277‑2 Grade ZSt52‑3: High‑Strength, Cold‑Drawn Structural Steel for Dynamic Welded Applications

ZSt 52-3 as bright drawn fine grained high strength structural steel grade is used for dynamic loaded welded constructions up to a temperature of -20 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

20 - 22 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

600 - 620 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-20 - 0 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

-100.0 °C

37.6 W/(m·K)

20.0 °C

42.2 W/(m·K)

100.0 °C

43.2 W/(m·K)

200.0 °C

42.9 W/(m·K)

300.0 °C

41.2 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.6 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

-100.0 °C

12.9 mm²/s

20.0 °C

11.7 mm²/s

100.0 °C

11.2 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.4 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

1.82E-7 Ω·m

20.0 °C

2.47E-7 Ω·m

100.0 °C

2.96E-7 Ω·m

200.0 °C

3.68E-7 Ω·m

300.0 °C

4.55E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.75E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Aluminium

0.02 %

Carbon

0.2 %

Manganese

1.6 %

Phosphorus

0.04 %

Silicon

0.55 %

Sulfur

0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-2 Grade ZSt50-2: Cold‑Drawn or Turned, Soft‑Annealed Steel for High‑Performance Wear Parts
    2. EN 10277-2 Grade ZSt60-2: Cold‑Drawn, Soft‑Annealed Steel for High‑Strength, Wear‑Resistant Parts
    3. EN 10277-2 Grade ZSt70-2 – Cold Drawn/Turned, Soft‑Annealed High‑Carbon Steel
    4. EN 10277-2: Grade St 37-2 – Cold Drawn or Turned, Soft Annealed Steel
    5. EN 10277-2 Grade St 50-2: Cold-Drawn, Turned, Soft-Annealed Structural Steel for High-Strength Applications
    6. EN 10277-2 Grade St 60-2 – Cold Drawn, Turned & Soft Annealed Structural Steel
    7. EN 10277‑2 Grade St 70‑2: Cold‑Drawn, Turned, and Soft‑Annealed Structural Steel
    8. EN 10277‑2 Grade St 44‑2: Cold‑Drawn, Turned & Soft‑Annealed Steel for Low‑Temperature Welded Construction
    9. EN 10277-2 Grade St 44-3: Cold‑Drawn, Turned & Soft‑Annealed Fine‑Grained Steel
    10. EN 10277-2 Grade St52‑3: Cold‑Drawn or Turned & Soft‑Annealed High‑Strength Steel