EN 573-3 Grade 3.0205 H19 – Certified Aluminium Alloy Properties

Properties

General

Property	Value	Condition	Related Standards
Density	2.71 g/cm³	H19	EN 573-3, EN 485, EN 683

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	69.0 GPa	H19	EN 573-3, EN 485, EN 683
Hardness, Brinell	48.0 [-]	H19	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 1000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 1000 Series Aluminium
Shear modulus	25.9 GPa	H19	EN 573-3, EN 485, EN 683
Tensile strength	160.0 MPa	H19	EN 573-3, EN 485
	170.0 MPa	H19	EN 573-3, EN 683

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.17e-05 1/K	H19	EN 573-3, EN 485, EN 683
	20 °C	2.17e-05 1/K	H19	EN 573-3, EN 485, EN 683
	20 °C	2.35e-05 1/K	H19	EN 573-3, EN 485, EN 683
	20 °C	2.4399999999999997e-05 1/K	H19	EN 573-3, EN 485, EN 683
	20 °C	2.5399999999999997e-05 1/K	H19	EN 573-3, EN 485, EN 683
	100 °C	2.35e-05 1/K	H19	EN 573-3, EN 485, EN 683
	200 °C	2.4399999999999997e-05 1/K	H19	EN 573-3, EN 485, EN 683
	300 °C	2.5399999999999997e-05 1/K	H19	EN 573-3, EN 485, EN 683
Melting point		644.0 - 657.0 °C	H19	EN 573-3, EN 485, EN 683
Specific heat capacity		900.0 - 963.0 J/(kg·K)			Typical for Wrought 1000 Series Aluminium
Thermal conductivity		205.0 - 210.0 W/(m·K)	H19	EN 573-3, EN 485, EN 683

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	33000000.0 - 34000000.0 S/m	H19	EN 573-3, EN 485, EN 683
Electrical resistivity	2.94e-08 - 3.03e-08 Ω·m	H19	EN 573-3, EN 485, EN 683

Chemical properties

Property	Value	Condition	Related Standards
Aluminium	99.0 %	H19	EN 573-3, EN 485, EN 683
Copper	0.05 %	H19	EN 573-3, EN 485, EN 683
Magnesium	0.05 %	H19	EN 573-3, EN 485, EN 683
Manganese	0.05 %	H19	EN 573-3, EN 485, EN 683
Titanium	0.05 %	H19	EN 573-3, EN 485, EN 683
Zinc	0.1 %	H19	EN 573-3, EN 485, EN 683

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good
Corrosion properties	Seawater: sufficient, weathering: acceptable
Workability	Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H12) / very good (H12)