DIN 17200 Grade C50 Steel – Normalized/Normalized Formed (+N) for High‑Strength Vehicle and Machine Parts

Steel C 50 is suitable for parts in vehicle manufacturing, engine and machine engineering with higher strength and wear resistance requirements (e.g. shafts, hubs). Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

14 - 16 %

Elongation, transverse

20.0 °C

12 - 14 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

580 - 820 MPa

Tensile strength, transverse

20.0 °C

580 - 820 MPa

Yield strength

20.0 °C

290 - 355 MPa

Yield strength, transverse

20.0 °C

290 - 355 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 52 W/(m·K)

100.0 °C

43.4 - 50.6 W/(m·K)

200.0 °C

43.2 - 48.1 W/(m·K)

300.0 °C

41.4 - 45.7 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Manganese

0.6 - 0.9 %

Phosphorus

0.05 %

Silicon

0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
    2. DIN 17240 Grade C35 Steel – Normalized or Normalized‑Formed (+N) for Creep Resistance up to 400 °C
    3. DIN 2395‑3 Grade M22 Tubes – Normalized & Normalized‑Formed (N)
    4. DIN 2391-2: Grade St 30 Al Seamless Steel Tubes – Normalized or Formed (+N)
    5. DIN 17200 Grade C60 Steel – Normalized/Normalized Formed (N) for High Ductility & Wear Resistance
    6. DIN 17200 Grade C35 Steel – Normalized or Normalized Formed (N) for Automotive & Machinery Applications
    7. DIN 17200 Grade C40: Normalized or Normalized Formed Steel for Heavy-Duty Applications
    8. DIN 17200 Grade C45 – Normalized or Normalized‑Formed Steel for Automotive & Machinery Applications
    9. DIN 17200 Grade C55: Normalized or Normalized Formed Steel for High-Stress Applications
    10. DIN 17200: Grade C22 Normalized or Normalized Formed Steel – Properties & Applications