ASTM B316 Grade 2017 T4 Aluminum Alloy – Heat‑Treatable, High Strength & Corrosion‑Resistant
Aluminum ASTM 2017 is a heat treatable wrought alloy that offers decent strength, ductility, and good machinability. Aluminum ASTM 2017 offers more strength than Aluminum 2011, and has fair workability and corrosion resistance. As with many aluminum alloys, Aluminum ASTM 2017 should not be welded as it reduces the alloy’s corrosion resistance.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 10.0 % | T4 | ASTM B316 | Wire, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Shear strength | 225.0 MPa | T4 | ASTM B316 | Wire, Rod | |
Tensile strength | 380.0 MPa | T4 | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T4 | ASTM B316 | Wire, Rod |
Copper | 3.5 - 4.5 % | T4 | ASTM B316 | Wire, Rod |
Iron | 0.7 | T4 | ASTM B316 | Wire, Rod |
Magnesium | 0.4 - 0.8 % | T4 | ASTM B316 | Wire, Rod |
Manganese | 0.4 - 1.0 % | T4 | ASTM B316 | Wire, Rod |
Silicon | 0.2 - 0.8 % | T4 | ASTM B316 | Wire, Rod |
Titanium | 0.15 | T4 | ASTM B316 | Wire, Rod |
Zinc | 0.25 | T4 | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B316 Grade 3003 H14: High-Quality Aluminum Alloy for Corrosion Resistance & Strength
- ASTM B316 Grade 7075 – High-Strength Aerospace Aluminum Alloy
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B316 Grade 2017 Aluminum Alloy: Properties & Applications
- ASTM B316 Grade 3003O Aluminum Alloy: High Corrosion Resistance & Easy Welding
- ASTM B316 Grade 2017 Aluminum Alloy – Strength, Ductility & Machinability
- ASTM B316 Grade 5005 O – High-Performance Aluminum Alloy for Marine and Industrial Use
- ASTM B316 Grade 5052‑O Aluminum Alloy: Superior Corrosion Resistance & Welding Performance
- ASTM B211 Grade 2017 Aluminum Alloy – Heat‑Treatable, High Strength & Machinability
- ASTM B316 Grade 7075 T6 Aluminum Alloy – High Strength & Corrosion Resistance