EN 1706 Grade AC-41000 F: Aluminium Casting Alloy Properties
Aluminium casting alloy (sand casting, permanent mould casting)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.71 g/cm³ | Typical for Cast 4xx.x Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 71.0 - 75.0 GPa | Typical for Cast 4xx.x Series Aluminium | ||||
Hardness, Brinell | 50.0 [-] | F | EN 1706, EN 13195 | Casting | ||
20.0 °C | 50.0 [-] | F | EN 1706 | |||
Poisson's ratio | 0.33 [-] | Typical for Cast 4xx.x Series Aluminium | ||||
Tensile strength | 140.0 MPa | F | EN 1706, EN 13195 | Casting | ||
170.0 MPa | F | EN 1706, EN 13195 | Casting | |||
20.0 °C | 140.0 MPa | F | EN 1706 | |||
20.0 °C | 170.0 MPa | F | EN 1706 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | F | EN 1706, EN 13195 | Casting | |
100.0 °C | 2.3e-05 1/K | F | EN 1706, EN 13195 | Casting | ||
100 °C | 2.3e-05 1/K | F | EN 1706, EN 13195 | Casting | ||
Melting point | 565.0 - 630.0 °C | Typical for Cast 4xx.x Series Aluminium | ||||
Specific heat capacity | 963.0 J/(kg·K) | Typical for Cast 4xx.x Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 140.0 - 160.0 W/(m·K) | F | EN 1706, EN 13195 | Casting |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 19000000.0 - 25000000.0 S/m | F | EN 1706, EN 13195 | Casting |
Electrical resistivity | 4e-08 - 5.26e-08 Ω·m | F | EN 1706, EN 13195 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 95.05 % | F | EN 1706 | |
Copper | 0.1 % | F | EN 1706, EN 13195 | Casting |
Iron | 0.6 % | F | EN 1706 | |
0.60 % | F | EN 1706, EN 13195 | Casting | |
Lead | 0.05 % | F | EN 1706, EN 13195 | Casting |
Magnesium | 0.45 - 0.65 % | F | EN 1706, EN 13195 | Casting |
Manganese | 0.3 - 0.5 % | F | EN 1706, EN 13195 | Casting |
Nickel | 0.05 % | F | EN 1706, EN 13195 | Casting |
0.15 % | F | EN 1706 | ||
Silicon | 1.6 - 2.4 % | F | EN 1706, EN 13195 | Casting |
Tin | 0.05 % | F | EN 1706, EN 13195 | Casting |
Titanium | 0.05 - 0.2 % | F | EN 1706, EN 13195 | Casting |
0.15 - 0.2 % | F | EN 1706 | ||
Zinc | 0.1 % | F | EN 1706, EN 13195 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: good | |
| Corrosion properties | general: good | |
| General machinability | after thermal treatment: acceptable, as cast: good | |
| Processing methods | permanent mould casting, separately cast test sample | |
Metal
- EN 1706 Grade AC-41000 T6 – Premium Aluminium Casting Alloy
- EN 1706 Grade AC-43500 T5 Aluminium Casting Alloy – Superior Strength & Durability
- EN 1706 Grade AC-43500 T7 Aluminium Alloy for Pressure Die Casting
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-48100 T5 Aluminium Alloy – Specifications & Properties
- EN 1706 Grade AC-21200 T4 Aluminium Alloy – Properties & Applications
- EN 1706 Grade AC-71100 T1 Aluminium Casting Alloy – Properties & Standards
- EN 1706 AC-21200 T7 Aluminium Casting Alloy – High Strength & Precision