EN 1706 AC-21200 T7 Aluminium Casting Alloy – High Strength & Precision
Aluminium casting alloy (sand casting, permanent mould casting)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.8 g/cm³ | Typical for Cast 2xx.x Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 80.0 - 110.0 MPa | T7 | EN 1706 | Casting | |
Elastic modulus | 72.0 GPa | Typical for Cast 2xx.x Series Aluminium | |||
Hardness, Brinell | 110.0 [-] | T7 | EN 1706 | Casting | |
120.0 [-] | T7 | EN 1706 | Casting | ||
Poisson's ratio | 0.33 [-] | Typical for Cast 2xx.x Series Aluminium | |||
Tensile strength | 370.0 MPa | T7 | EN 1706 | Casting | |
410.0 MPa | T7 | EN 1706 | Casting |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | T7 | EN 1706 | Casting | |
100 °C | 2.3e-05 1/K | T7 | EN 1706 | Casting | ||
Melting point | 510.0 - 790.0 °C | Typical for Cast 2xx.x Series Aluminium | ||||
Specific heat capacity | 875.0 - 963.0 J/(kg·K) | Typical for Cast 2xx.x Series Aluminium | ||||
Thermal conductivity | 120.0 - 150.0 W/(m·K) | T7 | EN 1706 | Casting |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 16000000.0 - 23000000.0 S/m | T7 | EN 1706 | Casting |
Electrical resistivity | 4.34e-08 - 6.25e-08 Ω·m | T7 | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 93.29 % | T7 | EN 1706 | |
Copper | 4.0 - 5.0 % | T7 | EN 1706 | Casting |
Iron | 0.2 % | T7 | EN 1706 | |
0.20 % | T7 | EN 1706 | Casting | |
Lead | 0.03 % | T7 | EN 1706 | Casting |
Magnesium | 0.15 - 0.5 % | T7 | EN 1706 | Casting |
Manganese | 0.2 - 0.5 % | T7 | EN 1706 | Casting |
Nickel | 0.05 % | T7 | EN 1706 | Casting |
Silicon | 0.1 % | T7 | EN 1706 | Casting |
Tin | 0.03 % | T7 | EN 1706 | Casting |
Titanium | 0.1 % | T7 | EN 1706 | Casting |
Zinc | 0.1 % | T7 | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable | |
| Corrosion properties | general: not sufficient | |
| General machinability | after thermal treatment: excellent | |
| Processing methods | permanent mould casting, separately cast test sample | |
Metal
- EN 1706 Grade AC-41000 F: Aluminium Casting Alloy Properties
- EN 1706 Grade AC-41000 T6 – Premium Aluminium Casting Alloy
- EN 1706 Grade AC-43500 T5 Aluminium Casting Alloy – Superior Strength & Durability
- EN 1706 Grade AC-43500 T7 Aluminium Alloy for Pressure Die Casting
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-48100 T5 Aluminium Alloy – Specifications & Properties
- EN 1706 Grade AC-21200 T4 Aluminium Alloy – Properties & Applications
- EN 1706 Grade AC-71100 T1 Aluminium Casting Alloy – Properties & Standards