EN 573-3 Grade 3.3527 H112: Comprehensive Material Properties & Standards
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.71 g/cm³ | H112 | EN 573-3, EN 485, EN 755 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H112 | EN 573-3, EN 485, EN 755 | |
Hardness, Brinell | 50.0 [-] | H112 | EN 573-3, EN 755 | |
52.0 [-] | H112 | EN 573-3, EN 485 | ||
58.0 [-] | H112 | EN 573-3, EN 485 | ||
62.0 [-] | H112 | EN 573-3, EN 485 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 180.0 MPa | H112 | EN 573-3, EN 755 | |
190.0 MPa | H112 | EN 573-3, EN 485 | ||
200.0 MPa | H112 | EN 573-3, EN 485 | ||
210.0 MPa | H112 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3699999999999997e-05 1/K | H112 | EN 573-3, EN 485, EN 755 | |
100 °C | 2.3699999999999997e-05 1/K | H112 | EN 573-3, EN 485, EN 755 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 620.0 - 650.0 °C | H112 | EN 573-3, EN 485, EN 755 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 140.0 - 180.0 W/(m·K) | H112 | EN 573-3, EN 485, EN 755 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 - 25000000.0 S/m | H112 | EN 573-3, EN 485, EN 755 |
Electrical resistivity | 4e-08 - 5e-08 Ω·m | H112 | EN 573-3, EN 485, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.3 % | H112 | EN 573-3, EN 485, EN 755 |
Copper | 0.1 % | H112 | EN 573-3, EN 485, EN 755 |
Iron | 0.50 % | H112 | EN 573-3, EN 485, EN 755 |
Magnesium | 1.6 - 2.5 % | H112 | EN 573-3, EN 485, EN 755 |
Manganese | 0.5 - 1.1 % | H112 | EN 573-3, EN 485, EN 755 |
Silicon | 0.4 % | H112 | EN 573-3, EN 485, EN 755 |
Titanium | 0.1 % | H112 | EN 573-3, EN 485, EN 755 |
Zinc | 0.2 % | H112 | EN 573-3, EN 485, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: good | |
| Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12) | |
Metal
- EN 573-3 Grade 3.3315 H112 – Comprehensive Material Specifications
- EN 573-3 Grade 3.3326 H112 Aluminium – Density, Modulus, Strength & Standards
- EN 573-3 Grade 3.0285 H112: Comprehensive Material Properties
- EN 573-3 Grade 3.0515 H112 Aluminium – Key Properties & Standards
- EN 573-3 Grade 3.3316 H112: Detailed Material Properties & Standards
- EN 573-3 Grade 3.0257 H112 – Comprehensive Aluminium Alloy Properties
- EN 573-3 Grade 3.0275 H112 – Premium Steel for Advanced Applications
- EN 573-3 Grade 3.3555 H112 – Aluminium Alloy Specifications & Key Properties
- EN 573-3 Grade 3.3525 H112 Aluminium: Properties & Standards
- EN 573-3 Grade 3.0205 H112 – Detailed Properties & Standards