DIN 1652-3 Grade Ck15 Cold Drawn Steel – Superior Wear Resistance and Strength

The steel Ck 15 is used for increased wear loaded parts with higher core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 15 (e.g. levers, joints, gears). The lowest application amounts to -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

6 - 12 %

Hardness, Brinell

20.0 °C

143 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

370 - 540 MPa

Yield strength

20.0 °C

200 - 440 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

57.5 W/(m·K)

100.0 °C

55.7 W/(m·K)

200.0 °C

51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.12 - 0.18 %

Manganese

0.3 - 0.6 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1652-3 Grade 20MoCrS4 Cold-Drawn Steel: Ideal for Wear-Resistant Mechanical Components
    2. DIN 1652-3: Grade 22CrMoS3-5 Cold-Drawn Steel – High Strength & Durability for Automotive & Mechanical Applications
    3. DIN 1652-3 Grade 20Cr4 Cold-Drawn Steel: High-Performance Wear-Resistant Material
    4. DIN 1652-3 Grade 20CrS4 Cold‑Drawn Steel – High Wear Resistance & Superior Machinability
    5. DIN 1652-3 Grade 20MnCrS5 Cold-Drawn Steel – Superior Strength & Machinability
    6. DIN 1652-3 Grade 20MoCr4 Cold-Drawn Steel – High Strength & Durability
    7. 15CrNi6 Grade 15/20 Cold-Drawn Steel – Superior Strength & Toughness for Automotive & Mechanical Parts
    8. DIN 1652-3 Grade 16MnCr5 Cold-Drawn Steel – High Strength & Toughness for Automotive & Mechanical Applications
    9. DIN 1652-3 Grade 16MnCrS5 Cold Drawn Steel – High Strength & Precision
    10. DIN 1652-3 Grade 17Cr3 Cold-Drawn Steel – High Wear Resistance for Automotive & Mechanical Parts