AA Standards Grade 5154 (H34) – Comprehensive Material Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 130.0 MPa | H34 | AA Standards | |
Elastic modulus | 70.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
Hardness, Brinell | 73.0 [-] | H34 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 270.0 - 320.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
270.0 MPa | H34 | AA Standards, ASTM B210, ASTM B211 | ||
290.0 MPa | H34 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3899999999999998e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 590.0 - 645.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 126 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 19000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Electrical resistivity | 5.26e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Copper | 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Iron | 0.40 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Magnesium | 3.1 - 3.9 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Manganese | 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Silicon | 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Titanium | 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Zinc | 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |
Metal
- ASTM B211 Grade 5154 H34 – High Strength Aluminium Alloy
- ASTM B210 Grade 5154 H34 Aluminum Alloy – Key Properties & Applications
- AA Standards Grade 5050 H34 – Premium Aluminium Alloy Properties
- AA 5154 H36 Grade Aluminium Alloy – Specifications & Standards
- AA 5154 H38 Aluminium Alloy: Standards & Mechanical Properties
- AA 3004 H34 Aluminum Alloy: Comprehensive Standards & Specifications
- AA 5154 H112 Aluminium Standard – Comprehensive Property Overview
- AA 5154 H32 Aluminium Standard – Key Properties & Compliance
- AA Standards Grade 5154 O: Key Mechanical Properties & Specifications
- AA 5086 H34 Aluminum: Superior Strength & Corrosion Resistance for Structural Applications