AA Standards Grade 5050 H34 – Premium Aluminium Alloy Properties
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.69 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa | H34 | AA Standards | |
Elastic modulus | 69.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
Hardness, Brinell | 53.0 [-] | H34 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 170.0 - 215.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
170.0 MPa | H34 | AA Standards, ASTM B210, ASTM B483 | ||
190.0 MPa | H34 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
100 °C | 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 625.0 - 650.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 193 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 29000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Electrical resistivity | 3.45e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Copper | 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Iron | 0.70 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Magnesium | 1.1 - 1.8 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Manganese | 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Silicon | 0.4 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Zinc | 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O), poor (H32, H34), sufficient (H36, H38) | |
| Workability | general (condition): good (O, H32), acceptable (H34), poor(H36, H38) | |
Metal
- ASTM B483 Grade 5050 H34 – Premium 5050 Series Aluminum Alloy Specifications
- ASTM B210 Grade 5050 H34 Aluminum – Technical Specifications & Mechanical Properties
- AA 3004 H34 Aluminum Alloy: Comprehensive Standards & Specifications
- AA Standard Grade 5050 (H32): Specifications & Performance
- AA Standards Grade 5050 H36: Key Properties & Performance
- AA Standards Grade 5050 (H38) – Key Mechanical Properties & Specifications
- AA Standards Grade 5154 (H34) – Comprehensive Material Specifications
- AA 5050O Aluminium Alloy – Standards & Mechanical Properties
- AA 5086 H34 Aluminum: Superior Strength & Corrosion Resistance for Structural Applications
- AA 5052 H34 Aluminum Alloy – Premium Corrosion Resistance & Superior Welding