AA 5052 H34 Aluminum Alloy – Premium Corrosion Resistance & Superior Welding

Aluminum AA 5052 is a non-heat treatable alloy with excellent finishing qualities. AA 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.68 g/cm³	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending Fatigue Strength	125.0 MPa	H34	AA Standards
Elastic modulus	70.0 GPa	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Hardness, Brinell	68.0 [-]	H34	AA Standards
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa			Typical for Wrought 5000 Series Aluminium
Tensile strength	235.0 - 285.0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	235.0 MPa	H34	AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483
	260.0 MPa	H34	AA Standards

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	20 °C	2.38e-05 1/K	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
	100 °C	2.38e-05 1/K	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		605.0 - 650.0 °C	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Specific heat capacity		879.0 - 963.0 J/(kg·K)			Typical for Wrought 5000 Series Aluminium
Thermal conductivity		138 W/(m·K)	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	20000000.0 S/m	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Electrical resistivity	5e-08 Ω·m	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.15 - 0.35 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Copper	0.1 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Iron	0.40 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Magnesium	2.2 - 2.8 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Manganese	0.1 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Silicon	0.25 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547
Zinc	0.1 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547

Technological properties

Property
Brazing	general: limited brazing
Corrosion properties	Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere
General machinability	General: poor (O, H32), sufficient (H34, H36, H38)
Workability	general (condition): good (O), acceptable (H32, H34), poor(H36, H38)