DIN 1725-1 Grade 3.3309 O: High-Gloss Anodized Aluminum Alloy

The alloy AlRMg0,5 belongs to the standardised shining materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. If the high gloss surface is to be used with the material employment accordingly, is to be absolutely anodised afterwards.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.7 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	65.0 - 70.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Elongation	20.0 °C	20.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip	A10
	20.0 °C	23.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Hardness, Brinell	20.0 °C	23.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 5000 Series Aluminium
Shear modulus	20.0 °C	25.0 - 27.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Tensile strength	20.0 °C	80.0 - 120.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		2.2e-05 - 2.5e-05 1/K				Typical for Wrought 5000 Series Aluminium
Max service temperature		150.0 °C				Typical for Wrought 5000 Series Aluminium
Melting point		560.0 - 655.0 °C				Typical for Wrought 5000 Series Aluminium
Specific heat capacity		879.0 - 963.0 J/(kg·K)				Typical for Wrought 5000 Series Aluminium
Thermal conductivity	20.0 °C	215.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	33000000.0 - 35000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Electrical resistivity		3.3e-08 - 5e-08 Ω·m				Typical for Wrought 5000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Iron	0.008	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Magnesium	0.35 - 0.6 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Silicon	0.01	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Titanium	0.008	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Zinc	0.01	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip

Technological properties

Property
Workability	Good workability.

Property

Workability

Good workability.